MOVEMENT OF CORROSION OF PERICLASE-CHROMITE DIRECTLY BOUND REFRACTORIES IN THE SUCTION PIPE OF RH-VACUUM
https://doi.org/10.17073/1683-4518-2018-4-78-88
Abstract
The results of studies of refractory products based on the fused periclasechromite after service in the suction pipe of the RH vacuum at two metallurgical plants were reported. At one plant, the branch pipe was operated in contact with slag containing as a homogenizing additive fluorspar with an alumina slag-forming component, on the second with slag, for homogenization, which was used only by fluorspar. The duration of operation is 1550‒1800 min. It is established that the depth of infiltration of the slag melt components into the refractory depends on the type of homogenizing additive to the slag in the steel casting ladle. A slag containing a combination of fluorspar with an aluminous slag-forming additive penetrates the microstructure of the refractory to a greater depth, which leads to a change in the initial phase composition.
About the Authors
L. M. Aksel'rodRussian Federation
T. V. Yarushina
Russian Federation
A. A. Platonov
Russian Federation
A. O. Migashkin
Russian Federation
I. V. Anoshkin
Russian Federation
A. A. Bessol'nikov
Russian Federation
M. A. Yeroshin
Russian Federation
References
1. Минаев, Ю. А. Физикохимия в металлургии (Термодинамика. Гидродинамика. Кинетика) : уч. пособие для вузов / Ю. А. Минаев, В. В. Яковлев. ― М. : МИСиС, 2001. ― 320 с.
2. Аксельрод, Л. М. Огнеупоры для промышленных агрегатов и топок : Справочное издание. В двух книгах. Кн. 2. Служба огнеупоров / Л. М. Аксельрод [и др.]; под ред. И. Д. Кащеева [и др..] ― М. : Интермет Инжиниринг, 2002. ― 656 с.
3. Jones, P. T. A study of slag infiltrated magnesiachromite refractories using hydrid microwave heating /P. T. Jones, J. Vleugels, B. Blanpain [et al.] // J. Eur. Ceram. Soc. ― 2002. ― № 22. ― P. 903‒916.
4. Mosser, J. New high-quality MgO‒Cr2O3-bricks and Cr-free alternatives for the lining of RH/DH-vessels / J. Mosser, G. Buchebner, K. Dösinger // Veitsch Radex Rundschau. ― 1997. ― № 1. ― S. 11‒23.
5. Симонов, К. В. Огнеупоры на основе плавленого периклазохромитового материала для установок внепечного вакуумирования стали / К. В. Симонов, В. П. Чернявская, Л. Д. Бочаров [и др.] // Огнеупоры. ― 1976. ― № 8. ― C. 5‒12.
6. Суворов, С. А. Исследование в области физикохимических основ шлакового износа и технологии производства огнеупоров с участием периклаза, шпинелидов и глинозема : дис. ... докт. техн. наук / Суворов Станислав Алексеевич. ― Л., 1973. ― 38 с.
7. Балкевич, В. Л. Техническая керамика / В. Л. Балкевич. ― М. : Изд-во лит-ры по стр-ву, 1968. ― 277 с.
8. Кащеев, И. Д. Исследование масс системы MgO‒ Al2O3‒Cr2O3 / И. Д. Кащеев, Н. Ю. Новожилов, Н. Е. Мезенцева // Огнеупоры. ― 1980. ― № 10. ― C. 55‒58.
9. Ключаров, Л. В. Воздействие железистых расплавов на шпинелиднопериклазовые огнеупоры / Л. В. Ключаров, С. А. Суворов // Огнеупоры. ― 1966. ― № 3. ― C. 34‒41.
10. Керамика из высокоогнеупорных окислов : справочник ; под ред. Д. И. Полубояринова и Р. Я. Попильского. ― М. : Металлургия, 1977. ― 304 с.
11. Chesters, J. H. The measurement of reaction rates at high temperatures / J. H. Chesters, C. W. Parmelее // J. Am. Ceram. Soc. ― 1934. ― Vol. 17, № 13. ― P. 50‒59.
12. Jander, W. Jtscher of amorg allgenchem / W. Jander, W. Stamm // J. Am. Ceram. Soc. ― 1931. ― Vol. 199. ― P. 165‒182.
13. Кузнецов, Ю. Д. Об износе шпинелидных и шпинелидно-периклазовых огнеупоров под воздействием шлака / Ю. Д. Кузнецов, С. А. Суворов, А. Д. Мельников // Огнеупоры. ― 1975. ― № 3. ― С. 18.
14. Бережной, А. С. Сборник материалов по вопросам огнеупорной промышленности. № 12 / А. С. Бережной, В. М. Цынкина. ― М. : Металлургиздат, 1940.
15. Гладышевский, В. И. / В. И. Гладышевский, Е. Е. Черкашин, А. М. Ферсман // Неорганические материалы. ― 1965. ― Т. 1, вып. 6. ― С. 1354‒1401.
16. Ключаров, Л. В. Фазовые преобразования и изменения некоторых технических свойств высокоогнеупорных материалов системы MgO‒Al2O3‒Cr2O3 при воздействии CaO и Fe2O3 / Л. В. Ключаров // Тр. совещания по химии окислов при высоких температурах. ― Л., 1967. ― С. 114‒123.
17. Ровнушкин, В. А. Исследование влияния составов ковшевого шлака и огнеупоров на стойкость футеровки вакууматора RH / В. А. Ровнушкин, Э. А. Вислогузова, С. А. Спирин [и др.] // Бюл. Черная металлургия. ― 2005. ― № 4. ― С. 47‒50.
18. Ровнушкин, В. А. Механизм коррозии огнеупоров RH-вакууматора известковосиликатными шлаками различной основности / В. А. Ровнушкин, Л. М. Аксельрод, Л. А. Смирнов [и др.] // Новые огнеупоры. ― 2015. ― № 3. ― С. 65‒71. [Rovnushkin, V. A. RH-degasser refractory corrosion mechanism by lime-silica slags of different basicity /V. A. Rovnushkin, L. M. Aksel’rod, L. A. Smirnov [et al.] // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56,№ 2. ― P. 113‒118.]
19. Сибикин, А. Б. Влияние параметров структуры огнеупоров на их пропитку шлаком в условиях вакуумирования стали / А. Б. Сибикин, Е. С. Борисовский, Ф. С. Каплан [и др.] // Огнеупоры. ― 1990. ― № 10. ― С. 1‒7. [Sibikin, A. B. Effect of the structural parameters of refractories on their slag impregnation in the units used for vacuum refining of steels / A. B. Sibikin, E. S. Borisovskii, F. S. Kaplan [et al.] // Refractories. ― 1990. ― Vol. 31, № 9/10. ― Р. 543‒550.]
20. Ровнушкин, В. А. Исследование влияния составов ковшового шлака и огнеупоров на стойкость футеровки вакууматоров RH / В. А. Ровнушкин, Э. А. Вислогузова, С. А. Спирин [и др.] // Новые огнеупоры. ― 2005. ― № 3. ― С. 33‒36. [Rovnushkin, V. A. Composition of ladle slag and refractory materials and its effect on the wear resistance of the lining of an RH vacuum degasser / V. A. Rovnushkin, E. A. Visloguzova, S. A. Spirin [et al.] // Refractories and Industrial Ceramics. ― 2005. ― Vol. 46, № 3. ― P. 193‒196.]
21. Вислогузова, Э. А. Исследование влияния технологических факторов вакуумирования и качества периклазохромитовых огнеупоров на их износоустойчивость в футеровке вакуум-камер / Э. А. Вислогузова, А. А. Метелкин, Л. В. Зорихина [и др.] // Новые огнеупоры. ― 2006. ― № 9. ― С. 35‒38. [Visloguzova, Е. A. The effect of degassing technology parameters and the quality of periclasechromite refractories on their wear resistance in vacuum chamber lining / Е. A. Visloguzova, A. A. Metelkin, L. V. Zorikhina [et al.] // Refractories and Industrial Ceramics. ― 2006. ― Vol. 47, № 5. ― P. 288‒290.]
22. Мельхер, Ф. Механизмы коррозии огнеупоров, применяемых при внепечной обработке металла / Ф. Мельхер, Г. Гармус // Новые огнеупоры. ― 2011. ― № 2. ― С. 25‒30.
23. Бурмистрова, Е. В. Опыт эксплуатации циркуляционных вакууматоров № 1 и № 2 в условиях ККЦ / Е. В. Бурмистрова, Р. И. Абдрахманов, А. Ю. Игошин // Сталь. ― 2012. ― № 2. ― С. 22, 23.
24. Попель, С. И. Теория металлургических процессов : уч. пособие для вузов / С. И. Попель, А. И. Сотников, В. Н. Бороненков. ― М. : Металлургия, 1986. ― 463 с.
25. Френкель, Я. И. Кинетическая теория жидкостей / Я. И. Френкель. ― Л. : Наука, 1975. ― 487 с.
26. Wright, S. Viscosity of a CaO‒MgO‒Al2O3‒SiO2 melt containing spinel particles at 1646 K / S. Wright, L. Zhang, S. Sun, S. Jahanshahi // Metall. Mater. Trans. ― 2000. ― Vol. 31B. ― P. 97‒104.
27. Cho, M.-K. Investigation of slag-refractory interaction for the Ruhrstahl Heraeus (RH) vacuum degassing process in steelmaking / M.-K. Cho, M.-A. Van Ende, T.-H. Eun, I.-Н. Jung // J. Eur. Ceram. Soc. ― 2012. ― Vol. 32. ― P. 1503‒1517.
28. Явойский, В. И. Металлургия стали : уч. для вузов / В. И. Явойский, Ю. В. Кряковский, В. П. Григорьев [и др..] ― М. : Металлургия, 1983. ― 584 с.
29. Бигеев, А. М. Металлургия стали. Теория и технология плавки стали : учебник для вузов. 3-е изд., перераб. и доп. / А. М. Бигеев, В. А. Бигеев. ― Магнитогорск : МГТУ, 2000. ― 544 с.
30. Некрасов, И. В. Оценка вязкости гетерогенных оксидных расплавов / И. В. Некрасов // Молодой ученый. ― 2012. ― № 12. ― С. 95‒98.
31. Некрасов, И. В. Методика оценки вязкости промышленных шлаков / И. В. Некрасов, О. Ю. Шешуков, В. Н. Невидимов, С. А. Истомин // Изв. вузов. Черная металлургия. ― 2012. ― № 4. ― С. 21‒24.
32. Guo, M. Degradation mechanisms of magnesiachromite refractories by high alumina stainless steel slags under vacuum conditions / M. Guo, P. T. Jones, S. Parada [et al.] // J. Eur. Ceram. Soc. ― 2006. ― № 26. ― P. 3831‒3843.
33. Метелкин, А. А. Гомогенизация ковшевых шлаков в условиях ОАО «ЕВРАЗ НТМК» / А. А. Метелкин, О. Ю. Шешуков, И. В. Некрасов, Д. К. Егиазарьян // Теория и технология металлургического производства. Металлургия стали. ― 2014. ― № 1 (14). ― С. 28‒31.
34. Белянкин, Д. С. Физико-химические системы силикатной технологии / Д. С. Белянкин, В. В. Лапин, Н. А. Торопов ; под ред. Д. С. Белянкина. ― М. : Гос. изд-во лит-ры по строительным материалам, 1949. ― С. 251.
35. Пат. 2634140 Российская Федерация. Хромитопериклазовый огнеупор / Аксельрод Л. М., Турчин М. Ю., Ерошин М. А., Ярушина Т. В., Жильцова А. Г. ; заявл. 29.09.2016 ; опубл. 24.10.2017, Бюл. № 30.
Supplementary files
For citation: Aksel'rod L.M., Yarushina T.V., Platonov A.A., Migashkin A.O., Anoshkin I.V., Bessol'nikov A.A., Yeroshin M.A. MOVEMENT OF CORROSION OF PERICLASE-CHROMITE DIRECTLY BOUND REFRACTORIES IN THE SUCTION PIPE OF RH-VACUUM. NOVYE OGNEUPORY (NEW REFRACTORIES). 2018;(4):78-88. https://doi.org/10.17073/1683-4518-2018-4-78-88
Refbacks
- There are currently no refbacks.