RESEARCHES IN THE FIELD OF COMPOSITE HCBS AND OF THE REFRACTORY MATERIALS ON THEIR BASE IN THE AL2O3‒SIO2‒SIC SYSTEM. PART 1
https://doi.org/10.17073/1683-4518-2018-3-17-27
Abstract
The analysis is given in the article for the recent investigations in the field of the preparation of SiC-containing suspensions and of the materials on their base. The influence of the dispersion degree of the SiC additives in the composite Al2O3- SiO2‒SiC highly-concentrated ceramic bonding suspension with the predominantly high-alumina composition on the properties of the materials on their base was investigated after the burning within 1000‒1400 °C. The influence was studied of the burning temperature on the sample's shrinkage and growth, and on their porosity and bending strength. The samples showed the mass increase after the burning at 1200, 1300 and 1400°C which demonstrates the SiC oxidation with the SiO2 forming. The ultimate bending strength at the burning temperature of 1200 °C (110‒130 MPa) were reached at 1200 °C, the samples of all compositions showed the ultimate compression strength of 200‒425 MPa at the burning temperature 1200 °C. Ill. 8. Ref. 33. Tab. 1.
About the Authors
Yu. E. PivinskiiRussian Federation
P. V. Dyakin
Russian Federation
References
1. Кащеев, И. Д. Химическая технология огнеупоров / И. Д. Кащеев, К. К. Стрелов, П. С. Мамыкин. ― М. : Интермет инжиниринг, 2007. ― 752 с.
2. Гнесин, Г. Г. Карбидокремниевые материалы / Г. Г. Гнесин. ― М. : Металлургия, 1977. ― 215 c.
3. Алленштейн, И. Огнеупорные материалы. Структура, свойства, испытания : справочник / И. Алленштейн [и др.] ; под ред. Г. Роучка, Х. Вутнау ; пер. с нем. ― М. : Интермет Инжиниринг, 2010. ― 392 с.
4. Кайнарский, И. С. Карборундовые огнеупоры / И. С. Кайнарский, Э. В. Дегтярева. ― Харьков : Металлургия, 1963. ― 252 с.
5. Пивинский, Ю. Е. Неформованные огнеупоры. Т. 1. Общие вопросы технологии / Ю. Е. Пивинский. ― М. : Теплоэнергетик, 2003. ― 448 с.
6. Пивинский, Ю. Е. Керамические и огнеупорные материалы : избр. тр. в 2 т. Т. 2 / Ю. Е. Пивинский. ― СПб. : Стройиздат СПб, 2003. ― 668 с.
7. Гришпун, Е. М. Производство и служба высокоглиноземистых керамобетонов. 1. Набивные массы на основе модифицированных ВКВС боксита / Е. М. Гришпун, Ю. Е. Пивинский, Е. В. Рожков [и др.] // Огнеупоры и техническая керамика. ― 2000. ― № 3. ― C. 37‒41. [Grishpun, E. M. Production and service of high-alumina ceramic castables. 1. Ramming mixtures based on modified bauxite HCBS / E. M. Grishpun, Yu. Е. Pivinskii, E. V. Rozhkov [et al.] // Refractories and Industrial Ceramics. ― 2000. ― Vol. 41, № 3. ― P. 104‒108.]
8. Рожков, Е. В. Производство и служба высокоглиноземистых керамобетонов. 2. Свойства и служба виброналивных желобных масс на основе модифицированных ВКВС боксита / Е. В. Рожков, Ю. Е. Пивинский, М. З. Нагинский [и др.] // Огнеупоры и техническая керамика. ― 2001. ― № 5. ― C. 37‒44. [Rozhkov, E. V. Production and service of high-alumina ceramic castables. 2. Properties and service of vibration-placed castables based on bauxite–modified highly concentrated binding suspensions (HCBS) for use in blast–furnace runners / E. V. Rozhkov, Yu. Е. Pivinskii, M. Z. Naginskii [et al.] // Refractories and Industrial Ceramics. ― 2001. ― Vol. 42, № 5/6. ― P. 209‒215.]
9. Пивинский, Ю. Е. ВКВС и керамобетоны. Основные этапы развития / Ю. Е. Пивинский // Новые огнеупоры. ― 2003. ― № 2. ― C. 28‒39. [Pivinskii, Yu. E. Highly conсеntrаted ceramic binding suspensions (HCBS) and ceramic castables. Stages in research and development / Yu. E. Pivinskii // Refractories and Industrial Ceramics. ― 2003. ― Vol. 44, № 3. ― P. 152‒160.]
10. Пивинский, Ю. Е. Разработка технологий, производство и служба формованных и неформованных огнеупоров на основе ВКВС / Ю. Е. Пивинский, Е. М. Гришпун, А. М. Гороховский // Новые огнеупоры. ― 2015. ― № 5. ― C. 29‒39. [Pivinskii, Yu. E. Engineering, manufacturing, and servicing of shaped and highly conсеntrаted ceramic binding suspensions / Yu. E. Pivinskii, E. M. Grishpun, A. M. Gorokhovskii // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56, № 3. ― P. 245‒253.]
11. Пивинский, Ю. Е. Реология дисперсных систем, ВКВС и керамобетоны. Элементы нанотехнологий в силикатном материаловедении : избр. тр. в 3 т. Т. 3 / Ю. Е. Пивинский. ― СПб. : Политехника, 2012. ― 682 с.
12. Pivinskii, Yu. E. Unshaped and shaped refractories based on and highly conсеntrаted ceramic binding suspensions (HCBS) / Yu. E. Pivinskii, E. V. Rozhkov // Stahl und Eisen. ― 2001. Special. September. ― P. 133 (44th International Colloquium on Refractories).
13. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 9. Получение и свойства смешанных ВКВС состава: плавленый бокситокорунд, квaрцевое стекло, реактивный глинозем. Дилатометрические исследования материалов на их основе / Ю. Е. Пивинский, П. В. Дякин, А. Ю. Колобов // Новые огнеупоры. ― 2017. ― № 2. ―C. 39‒45. [Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 9. Preparation and properties of mixed HCBS composition: fuzed bauxite-corundum, quartz glass, reactive alumina. Dilatometric study of materials based on them / Yu. E. Pivinskii, P. V. Dyakin, A. Yu. Kolobov // Refractories and Industrial Ceramics. ― 2017. ― Vol. 58, № 1. ― P. 103‒108.]
14. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 10. Влияние температуры обжига на свойства материалов, полученных на основе ВКВС смешанного состава: плавленый бокситокорунд, кварцевое стекло, реактивный глинозем / Ю. Е. Пивинский, П. В. Дякин, А. М. Гороховский, Л. В. Остряков // Новые огнеупоры. ― 2017. ― № 4. ― C. 37‒43. [Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 10. Effect of firing temperature on properties of materials prepared based on mixed composition HCBS from fuzed bauxite-corundum, quartz glass, and reactive alumina / Yu. E. Pivinskii, P. V. Dyakin, A. M. Gorokhovskii, L. V. Ostryakov // Refractories and Industrial Ceramics. ― 2017. ― Vol. 58, № 2. ― P. 227‒232.]
15. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 11. ВКВС композиционного состава: плавленый корундобоксит, спеченный боксит, кварцевое стекло и некоторые свойства материалов на их основе / Ю. Е. Пивинский, П. В. Дякин, Л. В. Остряков // Новые огнеупоры. ― 2017. ― № 8. ― C. 57‒63. [Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on highalumina HCBS. Part 11. Composite composition HCBS (fuzed corundum-bauxite, sintered bauxite, quartz glass) and some properties of mater ia ls based upon them / Yu. E. Pivinskii, P. V. Dyakin, L. V. Ostryakov // Refractories and Industrial Ceramics. ― 2017. ― Vol. 58, № 4. ― P. 450‒456.]
16. Пивинский, Ю. Е. Высококонцентрированные керамические вяжущие суспензии. Исходные материалы, свойства и классификация / Ю. Е. Пивинский // Огнеупоры. ― 1987. ― № 4. ― С. 8‒20. [Pivinskii, Yu. E. Highly conсеntrаted ceramic binding suspensions. Raw materials properties and classification / Yu. E. Pivinskii // Refractories. ― 1987. ― Vol. 28, № 3/4. ― P. 179‒190.]
17. Пивинский, Ю. Е. Керамические вяжущие и керамобетоны / Ю. Е. Пивинский. ― М. : Металлургия, 1990. ― 270 с.
18. Дякин, П. В. Реологические и физико-химические свойства ВКВС и керамобетонов в системе Al2O3‒SiO2‒SiC / П. В. Дякин, Ю. Е. Пивинский // Фундаментальные исследования и новые технологии в строительном материаловедении : тез. докл. Всесоюз. конф., Белгород, 1989. Ч. 2. ― С. 34, 35.
19. А. c. 1638970 СССР. Керамобетонная масса для вибролитья / П. В. Дякин, Ю. Е. Пивинский, Ф. С. Каплан [и др.] ; заявл. 03.05.89 ; опубл. 01.12.90.
20. А. c. 1658590 СССР. Сырьевая смесь для получения высококонцентрированной суспензии / П. В. Дякин, Ю. Е. Пивинский, Н. А. Давыдов [и др.] ; заявл.26.07.89 ; опубл. 22.02.91.
21. А. c. 1715771 СССР. Способ получения безобжиговой керамики / П. В. Дякин, Ю. Е. Пивинский, Ф. С. Каплан [и др.] ; заявл. 25.12.89 ; опубл. 01.11.91.
22. Пивинский, Ю. Е. Литые (саморастекающиеся) керамобетоны. 3. Реотехнологические свойства формовочных систем для получения карбидкремниевых керамобетонов / Ю. Е. Пивинский, М. А. Скуратов // Огнеупоры и техническая керамика. ― 2000. ― № 11. ― C. 32‒36. [Pivinskii, Yu. E. Cast (Sеlf-Flow) ceramic castables. 3. Rheotechnological properties of molding systems for fabrication of silicon carbide ceramic castables / Yu. E. Pivinskii, M. A. Skuratov // Refractories and Industrial Ceramics. ― 2000. ― Vol. 41, № 11. ― P. 401‒404.]
23. Скуратов, М. А. Литые (саморастекающиеся) керамобетоны. 4. Растекаемость формовочных систем и некоторые свойства муллитокарбидкремниевых керамобетонов / М. А. Скуратов, Ю. Е. Пивинский // Огнеупоры и техническая керамика. ― 2001. ― № 1. ― C. 25‒31. [Skuratov, M. A. Cast (sеlf‒flow) ceramic castables. 4. Spreadability of molding systems and some properties of mullit-silicon carbide ceramic castables / M. A. Skuratov, Yu. E. Pivinskii // Refractories and Industrial Ceramics. ― 2001. ― Vol. 42, № 1/2. ― P. 23‒29.]
24. Пивинский, Ю. Е. Реологические и вяжущие свойства высокоглиноземистых суспензий / Ю. Е. Пивинский, П. Л. Митякин // Огнеупоры. ― 1981. ― № 5. ― С. 48‒52. [Pivinskii, Yu. E. Rheological and binding properties of high-alumina suspensions / Yu. E. Pivinskii, P. L. Mityаkin // Refractories. ― 1981. ― Vol. 22, № 3/4. ― Р. 292‒297.]
25. Oliveira I. R. Deflocculation of Al2O3‒SiC suspentions / I. R. Oliveira, P. Sepulveda, V. C. Pandolfelli // Am. Ceram. Soc. Bull. ― 2001. ― Vol. 80, № 2. ― P. 47‒53.
26. Пивинский, Ю. Е. Реологические и технологические свойства смешанных суспензий на основе огнеупорных компонентов / Ю. Е. Пивинский, А. И. Наценко // Огнеупоры. ― 1974. ― № 11. ― С. 49‒55. [Pivinskii, Yu. E. Rheological and technological properties of mixed suspensions of refractory components/ Yu. E. Pivinskii, A. I. Natsenko // Refractories. ― 1974. ― Vol. 15, № 11/12. ― P. 710‒716.]
27. Шмурадко, В. Т. Физико-химические особенности технологии муллитокорундовых материалов / В. Т. Шмурадко, О. В. Роман, А. Ф. Ильющенко [и др.] // Огнеупоры и техническая керамика. ― 2008. ― № 7. ― С. 3‒10.
28. Дороганов, В. А. Высококонцентрированные керамические вяжущие суспензии на основе карбида кремния / В. А. Дороганов, Ю. Н. Трепалина // Новые огнеупоры. ― 2010. ― № 8. ― С. 50‒52. [Doroganov, V. A. Highly concentrated ceramic binder suspensions based on silicon carbide / V. A. Doroganov, Yu. N. Trepalina // Refractories and Industrial Ceramics. ― 2010. ― Vol. 51, № 4. ― P. 302‒304.]
29. Дороганов, В. А. Огнеупорные материалы на основе искусственных керамических вяжущих суспензий карбидкремниевого состава / В. А. Дороганов, Н. А. Перетокина, Е. А. Дороганов [и др.] // Вестник БГТУ им. В. Г. Шухова. ― 2013. ― № 4. ― С. 156‒160.
30. Дороганов, В. А. Исследование наномодифицированных вяжущих карбида кремния и композитов на их основе / В. А. Дороганов, Н. А. Перетокина, Е. А. Дороганов [и др.] // Новые огнеупоры. ― 2014. ― № 9. ― С. 44‒47. [Doroganov, V. A. Study of nano-differentiated silicon carbide binders and composites based on them / V. A. Doroganov, N. A. Peretokina, E. A. Doroganov [et al.] // Refractories and Industrial Ceramics. ― 2014. ― Vol. 55, № 5. ― P. 465‒468.
31. Зайцев, С. В. Исследование свойств наносодержащих искусственных керамических вяжущих в системе Al2O3‒SiO2‒SiC / С. В. Зайцев, В. А. Дороганов, Е. А. Дороганов, Е. И. Евтушенко // Новые огнеупоры. ― 2016. ― № 10. ― С. 32‒36. [Zaitsev, S. V. Study of artificial ceramic binder properties in the system Al2O3‒SiO2‒SiC / S. V. Zaitsev, V. A. Doroganov, E. I. Evtushenko // Refractories and Industrial Ceramics. ― 2016. ― Vol. 57, № 5. ― P. 526‒530.]
32. Зайцев, С. В. Исследование искусственных керамических вяжущих муллитокарбидкремниевого состава и композитов на их основе / С. В. Зайцев, В. А. Дороганов, Е. А. Дороганов, Е. И. Евтушенко // Новые огнеупоры. ― 2017. ― № 2. ― С. 46‒49. [Zaitsev, S. V. Study of artificial ceramic binders of mullite-silicon carbide composition and composites based on them / S. V. Zaitsev, V. A. Doroganov, E. A. Doroganov, E. I. Evtushenko // Refractories and Industrial Ceramics. ― 2017. ― Vol. 58, № 1. ― P. 109‒112.]
33. Гришпун, Е. М. ВКВС и керамобетоны. Прорыв в технологии огнеупоров XXI века / Е. М. Гришпун, Ю. Е. Пивинский // Новые огнеупоры. ― 2002. ― № 2. ― С. 28‒33.
Supplementary files
For citation: Pivinskii Y.E., Dyakin P.V. RESEARCHES IN THE FIELD OF COMPOSITE HCBS AND OF THE REFRACTORY MATERIALS ON THEIR BASE IN THE AL2O3‒SIO2‒SIC SYSTEM. PART 1. NOVYE OGNEUPORY (NEW REFRACTORIES). 2018;(3):17-27. https://doi.org/10.17073/1683-4518-2018-3-17-27
Refbacks
- There are currently no refbacks.