PERICLASE-CHROMITE REFRACTORIES STRUCTURE AFTER THE WORKING LIFE IN THE FURNACES FOR THE SULFIDE RAW MATERIAL PROCESSING
https://doi.org/10.17073/1683-4518-2017-10-3-7
Abstract
The periclase-chromite refractories chemical and mineral compositions were investigated both before and after their overhaul period in the furnace for the sulfide raw materials processing. It was shown that dusty gas has an effect over the refractories composition and structure, causing the surface layer saturation by both the dust and the gas components. Copper, zinc and lead penetrate at a depth up to 5 mm, whereas the traces of the elevated sulfur level associated with the sulfates Fe12S11O51, MgSO4 and PbSO4, formation were found in 20 mm-layer. Waste refractories can be used both for the lining brickwork at the non-critical components of thermal units and kilns, and as the refractory powder to prepare the gun mixtures. Ill. 4. Ref. 10. Tab. 2.
About the Authors
A. M. KlyushnikovRussian Federation
K. V. Pikulin
Russian Federation
V. V. Belyaev
Russian Federation
E. N. Selivanov
Russian Federation
A. B. Lebed'
Russian Federation
L. Yu. Udoeva
Russian Federation
References
1. Ванюков, А. В. Комплексная переработка медного и никелевого сырья: учебник для вузов / А. В. Ванюков, Н. И. Уткин. ― Челябинск : Металлургия, Челяб. отд., 1988. ― 432 с.
2. Огнеупорное производство : справочник : в 2 т. Т. 2 ; под ред. Д. И. Гавриша. ― М. : Металлургия, 1965. ― 584 с.
3. Щекина, Т. И. Сравнительное исследование устойчивости хромитопериклазовых и периклазоуглеродистых огнеупоров при их взаимодействии с расплавами никелевого производства (экспериментальные данные). 1. Поведение хромитопериклазовых огнеупоров в присутствии металлошлакового и шлакового рас- плавов / Т. И. Щекина, А. М. Батанова, Т. Н. Курбыко [и др.] // Новые огнеупоры. ― № 11. ― 2014. ― С. 31‒43. Shchekina, T. I. Comparative study of chromitepericlase and periclase-carbon refractory stability during reaction with nickel production melts (experimental data). 1. Behavior of chromite-periclase refractories in the presence of metal-slag and slag melts / T. I. Shchekina, A. M. Batanova, T. N. Kurbyko [et al.] // Refractories and Industrial Ceramics. ― 2015. ― Vol. 55, № 6. ― Р. 526‒528.
4. Кожин, В. Г. Повышение стойкости футеровки пирометаллургических агрегатов ОАО «Святогор» / В. Г. Кожин, В. В. Беляев, Е. Н. Селиванов // Новые огнеупоры. ― 2003. ― № 10. ― С. 22‒25. Kozhin, V. G. Improving the refractory lining durability of pyrometallurgical plants in service at the Svyatogor Joint-Stock Co / V. G. Kozhin, V. V. Belyaev, E. N. Selivanov // Refractories and Industrial Ceramics. ― 2004. ― Vol. 45, № 4. ― P. 228‒231.
5. Кильский, А. Изучение коррозии периклазохромитовых огнеупоров для футеровки медеплавильных конвертеров / А. Кильский, Л. Обшинска, Й. Мондкевич // Огнеупоры и техническая керамика. ― 2012. ― № 11/12. ― С. 73‒76.
6. Селиванов, Е. Н. Пропитывание периклазохромитовой футеровки никелевым штейном / Е. Н. Селива- нов // Огнеупоры и техническая керамика. ― 1995. ― № 6. ― С. 28, 29. Selivanov, E. N. Impregnation of a periclasechromite lining with nickel matte / E. N. Selivanov // Refractories. ― 1995. ― Vol. 36, № 6. ― Р. 191‒193.
7. Кащеев, И. Д. Свойства и применение огнеупоров : справочное издание / И. Д. Кащеев. ― М. : Теплотех- ник, 2004. ― 352 с.
8. Fotoyi, N. Z. Interaction of MgO‒MgR2O4 (R: Al, Cr, Fe) with SO2-containing gasses / N. Z. Fotoyi, R. H. Eric // Southern African Institute of Mining and Metallurgy. ― Johannesburg, 6‒9 March 2011. ― P. 373‒388.
9. Аксельрод, Л. М. Исследование износа хромито- периклазовых огнеупоров в реакционной зоне вельц- печи цинкового производства // Л. М. Аксельрод, Т. В. Ярушина, И. Г. Марясев, В. Л. Нечунаев // Цветные металлы. ― 2016. ― № 12. ― С. 14‒19.
10. Аксельрод, Л. М. Износ хромитопериклазовых огне- упоров в реакционной зоне вельц-печи цинкового производства / Л. М. Аксельрод, Т. В. Ярушина, И. Г. Марясев [и др.] // Новые огнеупоры. ― 2016. ― № 11. ― С. 5‒11. Aksel’rod, L. M. Chromite-periclase refractory wear in zinc production waelz kiln reaction zone / L. M. Aksel’rod, T. V. Yarushina, I. G. Maryasev [et al.] // Refractories and Industrial Ceramics. ― 2016. ― Vol. 57, № 6. ― Р. 563‒568.
Supplementary files
For citation: Klyushnikov A.M., Pikulin K.V., Belyaev V.V., Selivanov E.N., Lebed' A.B., Udoeva L.Y. PERICLASE-CHROMITE REFRACTORIES STRUCTURE AFTER THE WORKING LIFE IN THE FURNACES FOR THE SULFIDE RAW MATERIAL PROCESSING. NOVYE OGNEUPORY (NEW REFRACTORIES). 2017;(10):3-7. https://doi.org/10.17073/1683-4518-2017-10-3-7
Refbacks
- There are currently no refbacks.