THE POWDER COMPACT'S STRUCTURE. PART II. METHODS OF INCREASING PARTICLE PACKING UNIFORMITY
https://doi.org/10.17073/1683-4518-2014-6-34-45
Abstract
The methods of increasing uniformity of powder compact structure are regarded in the articles which are categorized into technological and structural groups. When regarding the technological group the emphasis was placed on ingenious approaches such as compact deformation and two-step sintering. Among the structural group both the method of compact uniformity increasing by means of ordered structures forming out of sintered powder and the method using the powders with internal nanostructure were distinguished. Ill. 21. Ref. 22. Tab. 1.
About the Author
A. V. GalakhovRussian Federation
References
1. Galakchov, A. V. Influence of pore structure inhomogeneities in green compacts on strength and reliability of Y-TZP / A. V. Galakchov, V. Ja. Shevchenko // J. Europ. Ceram. Soc. — 1990. — Vol. 6, № 5. — P. 317-322.
2. Галахов, А. В. Влияние давления формования на спекаемость субмикронных порошков тетрагонального диоксида циркония / А. В. Галахов, С. В. Куцев, В. А. Крючков [и др.] // Огнеупоры. — 1993. — № 2. — С. 5-11.
3. Cameron, C. P. Better Sintering through Green-State Deformation Processing / C. P. Cameron, R. Raj // J. Amer. Ceram. Soc. — 1990. — Vol. 73, № 7. — P. 2032-2037.
4. Frank, J. Microstructure refinement of sintered alumina by a two-step sintering technique / J. Frank, T. Lin, L. C. De Jonghe [et al.] // J. Amer. Ceram. Soc. — 1997. — Vol. 80, № 9. — P. 2269-2277.
5. Галахов, А. В. Структура порошкового компакта. Часть 1. Неоднородность упаковки частиц / А. В. Галахов // Новые огнеупоры. — 2014. — № 5. — C. 22-32.
6. Галахов, А. В. Неоднородность упаковки в порошковых компактах и прочность получаемой из них керамики / А. В. Галахов, Е. В. Цибайло // Огнеупоры и техническая керамика. — 1997. — № 5. — С. 14-19.
7. Nandiyanto, Asep Bayu Dani. Progress in developing spray-drying methods for the production of controlled morphology particles: From the nanometer to submicrometer size ranges / Asep Bayu Dani Nandiyanto, Kikuo Okuyama // Advanced Powder Technology. — 2011. — Vol. 22. — P. 1-19.
8. Ishizawa, Hitoshi. Homogeneous Y2O3-stabilized ZrO2 powder by spray pyrolysis method / Hitoshi Ishizawa, Osamu Sakurai, Nobuyasu Mizutani [et al.] // Am. Ceram. Soc. Bull. — 1986. — Vol. 65, №10. — P. 1399-1404.
9. Галахов, А. В. Наноструктурированные порошки для керамики / А. В. Галахов, Л. В. Виноградов, В. И. Антипов, А. Г. Колмаков // Российские на-нотехнологии. — 2011. — T. 6, № 9/10. — С. 131-135.
10. Tani, Takao. Dynamics of hollow and solid alumina particle formation in spray flames / Takao Tani, Kazumasa Takatori, S. E. Pratsinis // J. Amer. Ceram. Soc. — 2004. — Vol. 87, № 3. — P. 523-525.
11. Baranwal, R. Flame spray pyrolysis of precursors as a route to nano-mullite powder: Powder characterization and sintering behavior / R. Baranwal, M. P. Villar, R. Garcia [et al.] // J. Amer. Ceram. Soc. — 2001. — Vol. 84, № 5. — P. 951-961.
12. Kodas, Т. T. Aerosol flow reactor production of fine YlВа2Сu3О7 powder: Fabrication of superconducting ceramics / Т. T. Kodas, E. M. Engler, V. Y. Lee [et al.] / Appl. Phys. Lett. — 1988. — Vol. 52, № 19. — P. 1622-1624.
13. Slamovich, E. B. Spherical zirconia particles via electrostatic atomization: Fabrication and sintering characteristics / E. B. Slamovich, F. F. Lange // Mater. Res. Soc. Symp. Proc. — 1988. — Vol. 121. — Р. 257-262.
14. Галахов, А. В. Особенности спекания аэрозольных порошков / А. В. Галахов // Огнеупоры и техническая керамика. — 1999. — № 1/2. — С. 29-33.
15. Галахов, А. В. Спекание наноструктурированных порошков / А. В. Галахов, Л. В. Виноградов, В. И. Антипов [и др.] // Новые огнеупоры. — 2011. — № 5. — С. 16-22.
16. Tsukuma, K. Mechanical properties and thermal stability of CeO2 containing tetragonal zirconia polycrystals / K. Tsukuma // Amer. Ceram. Soc. Bull. — 1986. — Vol. 65, № 10. — Р. 1386-1389.
17. Tsukuma, K. Strength, fracture toughness and Vickers hardness of CeO2-stabilized tetragonal ZrO2 polycrystals (Ce-TZP) / K. Tsukuma, M. Shimada // J. Mater. Sci. — 1985. — Vol. 20. — Р. 1178-1184.
18. Антипов, В. И. Трансформационно-упрочненная ZrO2-CeO2 керамика на основе порошков, синтезированных методом ультразвукового распылительного пиролиза / В. И. Антипов, А. В. Галахов, Л. В. Виноградов [и др.] // Перспективные материалы. — 2011. — № 1. — С. 53-58.
19. Галахов, А. В. Композиционные порошки оксида алюминия с 15 % оксида циркония для конструкционной керамики / А. В. Галахов, Н. П. Абрамова, А. Фомина // Керамика в народном хозяйстве. — М. : ВИМИ, 1994.
20. Ikesue, A. Synthesis of Advanced Ceramics Lasers / A. Ikesue, Y. L. Aung // J. Amer. Ceram. Soa — 2006. — Vol. 89, № 6. — Р. 1936-1944.
21. Maitre, A. Effect of silica on the reactive sintering of polycrystalline Nd : YAG ceramics / A. Maitre, C. Salle, R. Bulesteix [et al.] // J. Amer. Ceram. So^ — 2008. — Vol. 91, № 2. — Р. 406-413.
22. Галахов, А. В. Наноструктурированные аэрозольные порошки алюмоиттриевого граната для лазерной поликристаллической керамики / А. В. Галахов, Л. В. Виноградов, В. И. Антипов [и др.] // Перспективные материалы. — 2009. — № 3. — С. 33-37.
Supplementary files
For citation: Galakhov A.V. THE POWDER COMPACT'S STRUCTURE. PART II. METHODS OF INCREASING PARTICLE PACKING UNIFORMITY. NOVYE OGNEUPORY (NEW REFRACTORIES). 2014;(6):34-45. https://doi.org/10.17073/1683-4518-2014-6-34-45
Refbacks
- There are currently no refbacks.