THE INVESTIGATION OF SHAPED AND NON-SHAPED REFRACTORIES FORMATION ON BASE OF HIGH-ALUMINA HCBS. Part V. The firing temperature influence on the properties of the materials obtained out of the fireclay containing composite HCBS

Yu. E. Pivinskii; P. V. Dyakin; L. V. Ostryakov

doi:10.17073/1683-4518-2016-4-24-29

THE INVESTIGATION OF SHAPED AND NON-SHAPED REFRACTORIES FORMATION ON BASE OF HIGH-ALUMINA HCBS. Part V. The firing temperature influence on the properties of the materials obtained out of the fireclay containing composite HCBS

Yu. E. Pivinskii, P. V. Dyakin, L. V. Ostryakov

https://doi.org/10.17073/1683-4518-2016-4-24-29

Full Text:

Abstract

The shrinkage value and growth rate as well as the porosity and strength of the samples on base of the composite finely dispersed glass suspension (bauxite + FDGS) and on base of the composite FDGS with the fireclay additives were investigated depending on the firing temperature within 800‒1600 °С at long-term heat treatment (60 hours at 1350‒1400 °С). Depending on their composition the samples had low shrinkage within 0,4‒1,15 % at 1100‒1200 °С and significant increase (2,0‒2,7 %) due to the secondary mullite growth at 1300‒1500 °С.

Keywords

bauxite, corundum, fireclay, finely dispersed glass suspension (FDGS), HCBS, mullite formation, shrinkage, sintering, bending strength,

About the Authors

Yu. E. Pivinskii

Научно-внедренческая фирма «Керамбет-Огнеупор», ООО, Санкт-Петербург
Russian Federation

P. V. Dyakin

Санкт-Петербургский государственный технологический институт (технический университет), Санкт-Петербург
Russian Federation

L. V. Ostryakov

Динур ОАО, Первоуральск Свердловской обл.
Russian Federation

References

1. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 4. Влияние добавок огнеупорной глины на свойства ВКВС композиционного состава, отливок и материалов на их основе / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2016. ― № 2. ― С. 25‒33.

2. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 1. Высокоглиноземистый боксит как базовый сырьевой компонент / Ю. Е. Пивинский, П. В. Дякин, В. А. Перепелицын // Новые огнеупоры. ― 2015. ― № 8. ― С. 16‒23. Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on highalumina HCBS. Part 1. High-alumina bauxite as a basic raw material component / Yu. E. Pivinskii, P. V. Dyakin, V. A. Perepelitsyn // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56, № 4. ― P. 344‒350.

3. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 2. Характеристика исходных компонентов и отливок на основе ВКВС композиционного состава. Изучение начальной стадии процессов их спекания и муллитизации / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2015. ― № 10. ― С. 50‒57. Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on highalumina HCBS. Part 2. Properties of starting components and castings based on composite composition HCBS. Study of the initial stage of sintering and mullitization / Yu. E. Pivinskii, P. V. Dyakin // Refractories and Industrial Ceramics. ― 2016. ― Vol. 56, № 5. ― P. 544‒550.

4. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 3. Влияние температуры обжига на спекание и муллитизацию ма териалов, полученных на основе ВКВС композиционного состава / Ю. Е. Пивинский, П. В. Дякин, Л. В. Остряков // Новые огнеупоры. ― 2015. ― № 12. ― С. 25‒33.

5. Пивинский, Ю. Е. Исследования в области получения материалов на основе ВКВС плавленого кварца. Часть 1. Сопоставительная оценка и отличительные особенности технологий кварцевой керамики и огнеупоров / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2014. ― № 7. ― С. 33‒40. Pivinskii, Yu. E. Research in the area of preparing materials based on fuzed quartz HCBS. Part 1. Comparative evaluation and distinguishing features of quarts ceramic and refractory technology / Yu. E. Pivinskii, P. V. Dyakin // Refractories and Industrial Ceramics. ― 2014. ― Vol. 58, № 4. ― Р. 311‒317.

6. Пивинский, Ю. Е. Исследования в области получения материалов на основе ВКВС плавленого кварца. Часть 3. Изучение и совершенствование процесса центробежного формования / Ю. Е. Пивинский // Новые огнеупоры. ― 2015. ― № 3. ― С. 26‒37. Pivinskii, Yu. E. Research in the area of preparing materials based on fuzed quartz HCBS. Part 3. Study and improvement of centrifugal casting / Yu. E. Pivinskii // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56, № 2. ― P. 126‒135.

7. Пивинский, Ю. Е. Исследования в области получения материалов на основе ВКВС плавленого кварца. Часть 5. Влияние спекания на пористость и прочность материалов / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2015. ― № 6. ― С. 47‒55. Pivinskii, Yu. E. Research in the area of preparing materials based on fuzed quartz HCBS. Part 5. Effect of sintering on material, porosity and strength / Yu. E. Pivinskii, P. V. Dyakin // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56, № 3. ― P. 296‒303.

8. Пивинский, Ю. Е. Исследования в области получения материалов на основе ВКВС плавленого кварца. Часть 6. Влияние температуры обжига на спекание и кристобалитизацию материалов / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2015. ― № 7. ― С. 22‒31. Pivinskii, Yu. E. Research in the area of preparing materials based on fuzed quartz HCBS. Part 6. Effect of firing temperature on material sintering and cristobalitization / Yu. E. Pivinskii, P. V. Dyakin // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56, № 4. ― P. 366‒373.

9. Пивинский, Ю. Е. Разработка технологий, производство и служба формованных и неформованных огнеупоров на основе ВКВС / Ю. Е. Пивинский, Е. М. Гришпун, А. М. Гороховский // Новые огнеупоры. ― 2015. ― № 5. ― С. 29‒39. Pivinskii, Yu. E. Engineеring, manufacturing, and servicing of shaped and unshaped refractories based on highly concentrated ceramic binding suspensions / Yu. E. Pivinskii, E. M. Grishpun, A. M. Gorokhovskii // Refractories and Industrial Ceramics. ― 2015. ― Vol. 56, № 3. ― P. 245‒253.

10. Пивинский, Ю. Е. Керамические и огнеупорные материалы : избр. тр. В 3 т. Т. 2 / Ю. Е. Пивинский. ― СПб. : Стройиздат СПб., 2003. ― 668 с.

11. Пивинский, Ю. Е. Реология дисперсных систем, ВКВС и керамобетоны. Элементы нанотехнологий в силикатном материаловедении : избр. тр. В 3 т. Т. 3 / Ю. Е. Пивинский. ― Санкт-Петербург : Политехника, 2012. ― 682 c.

12. Бакунов, В. С. Керамика из высокоогнеупорных окислов / В. С. Бакунов, В. Л. Балкевич, А. С. Власов [и др.] ; под ред. Д. Н. Полубояринова и Р. Я. Попильского. ― М. : Металлургия, 1977. ― 304 с.

Supplementary files

For citation: Pivinskii Y.E., Dyakin P.V., Ostryakov L.V. THE INVESTIGATION OF SHAPED AND NON-SHAPED REFRACTORIES FORMATION ON BASE OF HIGH-ALUMINA HCBS. Part V. The firing temperature influence on the properties of the materials obtained out of the fireclay containing composite HCBS. NOVYE OGNEUPORY (NEW REFRACTORIES). 2016;(4):24-29. https://doi.org/10.17073/1683-4518-2016-4-24-29

Refbacks

There are currently no refbacks.

ISSN 1683-4518 (Print)

Username
Password