Corrosion resistance of refractory castables in dynamic conditions

V. A. Doroganov; E. A. Doroganov; A. V. Pilenko; S. A. Kemenov; S. V. Gnidash; R. Yu. Kuftyrev; E. S. Lukin

doi:10.17073/1683-4518-2022-9-57-61

Corrosion resistance of refractory castables in dynamic conditions

V. A. Doroganov, E. A. Doroganov, A. V. Pilenko, S. A. Kemenov, S. V. Gnidash, R. Yu. Kuftyrev, E. S. Lukin

https://doi.org/10.17073/1683-4518-2022-9-57-61

Full Text:

Abstract

Tests of corrosion resistance of refractory castables to borosilicate glass melt under dynamic conditions were carried out. A method for calculating various indicators characterizing the glass resistance of a refractory exposed to glass melt is presented. On the basis of the data obtained during the tests, the rates of linear corrosion of the submerged part of the samples and at the level of the melt mirror, the rate of bulk corrosion of materials and the relative index of glass resistance were calculated. Based on the analysis of the calculated data, the compositions of refractory castables were identified, which are characterized by high glass resistance, in comparison with other materials. Ill. 4. Ref. 11. Tab. 2.

Keywords

refractory castable, glass melt, linear corrosion rate, volumetric corrosion rate, glass resistance index, dynamic test method,

About the Authors

V. A. Doroganov

ФГБОУ ВО «Белгородский государственный технологический университет имени В. Г. Шухова»
Russian Federation

E. A. Doroganov

ФГБОУ ВО «Белгородский государственный технологический университет имени В. Г. Шухова»
Russian Federation

A. V. Pilenko

ФГБОУ ВО «Белгородский государственный технологический университет имени В. Г. Шухова»
Russian Federation

S. A. Kemenov

ФГБОУ ВО «Белгородский государственный технологический университет имени В. Г. Шухова»
Russian Federation

S. V. Gnidash

АО «Подольские огнеупоры»
Russian Federation

R. Yu. Kuftyrev

АО «Подольские огнеупоры»
Russian Federation

E. S. Lukin

ФГБОУ ВО «Российский химико-технологический университет имени Д. И. Менделеева»
Russian Federation

References

1. Pivinskii, Yu. E. Сement-free refractory concretes. Part 1. General information. HCBS and ceramic concretes / Y. E. Pivinskii // Refract. Ind. Ceram. ― 2020. ― Vol. 60, issue 5. ― P. 430‒438. Пивинский, Ю. Е. Бесцементные огнеупорные бетоны. Часть 1. Общие сведения. ВКВС и керамобетоны / Ю. Е. Пивинский // Новые огнеупоры. ― 2019. ― № 9. ― С. 14‒24.

2. Дороганов, В. А. Огнеупорные материалы на основе искусственных керамических вяжущих суспензий карбидокремниевого состава / В. А. Дороганов, Е. А. Дороганов, Е. И. Евтушенко [и др.] // Вестник БГТУ имени В. Г. Шухова. ― 2013. ― № 4. ― С. 156‒160.

3. Spear, K. E. Thermodynamic analysis of alumina refractory corrosion by sodium or potassium hydroxide in glass melting furnaces / K. E. Spear, M. D. Allendorf // J. Electrochem. Soc. ― 2002. ― № 149 (12). ― P. 551‒559.

4. Aksel, C. The microstructural features of an aluminamullite-zirconia refractory material corroded by molten glass / C. Aksel // Ceram. Int. ― 2002. ― № 29 (3). ― P. 305‒309.

5. Россихина, Г. С. Коррозионная стойкость огнеупорных изделий из низкоцементных бетонов для стекольного производства / Г. С. Россихина, В. В. Подхолюзин, Е. А. Дороганов, В. А. Дороганов // Стекло и керамика. ― 2006. ― № 11. ― С. 24‒28

6. Mulevanov, S. V. Aspects of the corrosion of refractories in structured aggressive media / S. V. Mulevanov, V. M. Nartsev, V. A. Doroganov, S. V. Zaitsev // Refract. Ind. Ceram. ― 2012. ― Vol. 53, issue 4. ― P. 226‒228. Мулеванов, С. В. Особенности коррозии огнеупорных материалов в структурированных агрессивных средах / С. В. Мулеванов, В. М. Нарцев, В. А. Дороганов, С. В. Зайцев // Новые огнеупоры. ― 2012. ― № 7. ― С. 42‒45.

7. Wanga, Z. Dynamic and static corrosion of alphaalumina bonded refractory in contact with molten sodalime-silica (SLS) glass / Z. Wanga, T. Maotsela, P. M. Toperesu [et al.] // Ceram. Int. ― 2019. ― № 45 (1). ― P. 725‒732.

8. Baudm, С. Dynamic corrosion of Al2О3‒ZrО2‒SiО2 and Cr2О3-containing refractories bу molten frits. Part I: macroscopic analysis / С. Baudm, E. Criado, J. J. Bakali, P. Pena // J. Eur. Ceram. Soc. ― 2011. ― № 31 (5). ― P. 697‒703.

9. Pena, P. Dynamic corrosion of Al2О3‒ZrО2‒SiО2 and Cr2О3-containing refractories bу molten frits. Part II: microstructural study / P. Pena, E. Criado, J. J. Bakali, C. Baudm // J. Eur. Ceram. Soc. ― 2011. ― № 31 (5). ― P. 705‒714.

10. Rossikhina, G. S. А study of the corrosion resistance of refractory concretes to a melt of borosilicate glassunder dynamic conditions / G. S. Rossikhina, V. A. Doroganov // Refract. Ind. Ceram. ― 2010. ― Vol. 51, № 2. ― Р. 67‒69. Россихина, Г. С. Изучение коррозионной стойкости огнеупорных бетонов к расплаву боросиликатного стекла в динамических условиях / Г. С. Россихина, В. А. Дороганов // Новые огнеупоры. ― 2010. ― № 4. ― С. 68‒70.

11. Remizov, M. B. Corrosion testing of baddeleyitecorundum and chromium oxide materials in aluminum phosphate glass melts / M. B. Remizov, P. V. Kozlov, A. A. Kazadaev [et al.] // Refract. Ind. Ceram. ― 2018. ― Vol. 59, № 1. ― Р. 1‒5. Ремизов, М. Б. Коррозионные испытания бадделеитокорундовых и хромоксидных материалов в расплавах алюмофосфатных стекол / М. Б. Ремизов, П. В. Козлов, А. А. Казадаев [и др.] // Новые огнеупоры. ― 2018. ― № 1. ― С. 3‒7.

Supplementary files

For citation: Doroganov V.A., Doroganov E.A., Pilenko A.V., Kemenov S.A., Gnidash S.V., Kuftyrev R.Y., Lukin E.S. Corrosion resistance of refractory castables in dynamic conditions. NOVYE OGNEUPORY (NEW REFRACTORIES). 2022;(9):57-61. https://doi.org/10.17073/1683-4518-2022-9-57-61

Refbacks

There are currently no refbacks.

ISSN 1683-4518 (Print)

Username
Password