Analysis of quality parameters of fused cast AZS refractories for glass-making furnaces
https://doi.org/10.17073/1683-4518-2021-4-3-9
Abstract
A comprehensive analysis of the quality parameters of fused-cast aluminum-zirconium-silicate (AZS) refractories for glass furnaces has been carried out. It is shown that the assessment of the quality of AZS refractories by the content of ZrO2 and density in them does not give an objective idea of their operational properties. Of fundamental importance are the chemical composition and behavior of the glass phase, which determine the volume and temperature of the onset of exudation. Among the most important conditions for obtaining high-quality AZS refractories, characterized by a melting volume of 2‒3 % of the glass phase and a melting start temperature above 1400 °C, include the oxidative melting technology and the content of impurities in the chemical composition of the refractory no more than 0,25‒0,30 %. The conditions for the service of AZS refractories in the melting basin and the working space of glass-melting furnaces are formulated. Their influence on the course of the exudation process, the corrosion resistance of refractories and the formation of defects in glass is shown. Ill. 2. Ref. 30. Tab. 4.
References
1. Dzyuzer, V. Ya. Electrofused AZS refractories for high-capacity glass-founding furnaces / V. Ya. Dzyuzer // Refract. Ind. Ceram. ― 2013. ― Vol. 54, № 4. ― Р. 304‒306. [Дзюзер, В. Я. Электроплавленые AZS-огнеупоры для высокопроизводительных стекловаренных печей / В. Я. Дзюзер // Новые огнеупоры. ― 2013. ― № 7. ― С. 50‒52.]
2. İzmirlioğlu, B. Glass melting furnace refractories and refractory related defects / B. İzmirlioğlu, S. Yılmaz // Journal of Chemical Technology and Metallurgy. ― 2015. ― Vol. 50, № 4. ― P. 404‒410.
3. Dzyuzer, V. Ya. Use of refractories in the melting tank of a high-production-capacity glass melting furnace / V. Ya. Dzyuzer // Refract. Ind. Ceram. ― 2019. ― Vol. 59, № 5. ― Р. 435‒440. [Дзюзер, В. Я. Служба огнеупоров в варочном бассейне высокопроизводительной стекловаренной печи / В. Я. Дзюзер // Новые огнеупоры. ― 2018. ― № 9. ― С. 3‒9.]
4. ГОСТ 23053‒ 78. Изделия огнеупорные бадделеито-корундовые для стекловаренных печей. Технические условия.
5. STANDART JC 493‒2015. Fused cast AZS Refractories for glass furnace: ICS 81.080 Q44. — The general specification of building materials in China.
6. SEFPRO. Products and Services for the Glass Industry : http://www.ru.sefpro.com.
7. RHI GLAS. Feuerfeste Werkstoffe für die Glasindustrie : http://www.rhi.com.
8. MOTIM. Fused Cast Refractories Ltd : http://www.motim.hu.
9. ZIRCOR Electrofusion s. a. AZS Fused Cast Refractories : http://www.zircor.com.
10. Luoyang Dayang Refractory : http://www.dyrefractory.com.
11. АО «Подольские огнеупоры» : info@podolskrefractories.com.
12. Попов, О. Н. Производство и применение плавленолитых огнеупоров / О. Н. Попов, П. Т. Рыбалкин, В. А. Соколов, С. Д. Иванов. ― М. : Металлургия, 1985. ― 256 с.
13. ASTM C 621–09 (2018). Standard Test Method for Isothermal Corrosion Resistance of Refractories to Molten Glass.
14. Walrod, D. How furnace operation affects AZS glassy phase exudation / D. Walrod // Glass Ind. ― 1990. ― Vol. 71, № 8. ― P. 19‒27.
15. Heidrich, R. Fused cast AZS glassy phase exudation: intrinsic or pathologic property? / R. Heidrich, A. Gupta // RHI Bulletin. ― 2011. ― № 2. ― P. 24‒28.
16. Fleischmann, B. Glassy phase segregation from AZS blocks / B. Fleischmann // Glass Science and Technology. ― 2005. ― Vol. 78, № 6. ― P. 295‒300.
17. Canaguier, J. How to reduce corrosion on fused-cast AZS / J. Canaguier // 16th Conference on the Electric Glass Melting. ― Prague : Czech Glass Society, 2016. ― 36 p.
18. ASTM C 1223‒19. Standard Test Method for Testing of Glass Exudation from AZS Fusion-Cast Refractories.
19. https://www.diytrade.com/china/pd/9843042/AZS_refractory_Glass_refractory.html.
20. Selkregg, K. Investigation of defects in high-quality glasses / K. Selkregg, A. Gupta // 64th Conference on Glass Problems : Ceramic Engineering and Science Proceedings. ― 2008. ― Vol. 25, № 1. ― P. 13‒32.
21. Van Dijk, F. A. G. Glass defects originating from glass melt/fused cast AZS refractory interaction / F. A. G. van Dijk. ― Eindhoven : Technische Universitet Eindhoven, 1994. ― 188 p.
22. Simurka, P. Corrosion of AZS refractories — source of defects in tableware glass / P. Simurka, J. Kraxner, P. Vrabel, T. Pauco // 76th Conference on Glass Problems. ― 2016 (may). ― P. 89‒102.
23. Selkregg, K. Characterization of glass defects arising in today’s evolving glass technologies / K. Selkregg // RHI Bulletin. ― 2014. ― № 2. ― P. 19‒26.
24. Walrod, D. A. Study of the driving force behind AZS glass phase exudation / D. A. Walrod // // Proceedings of the 49th Conference on Glass Problems: Ceramic Engineering and Science Proceedings. ― 2008. ― Vol. 10, № 3/4. ― P. 338‒347.
25. Дзюзер, В. Я. Проектирование энергоэффективных стекловаренных печей / В. Я. Дзюзер, В. С. Швыдкий. ― М. : Теплотехник, 2009. ― 340 с.
26. Дзюзер, В. Я. Граничные условия для расчета футеровки стекловаренной печи с инновационными параметрами технической эффективности / В. Я. Дзюзер, В. С. Швыдкий // Новые огнеупоры. ― 2015. ― № 12. ― С. 9‒12. [Дзюзер, В. Я. Граничные условия для расчета футеровки стекловаренной печи с инновационными параметрами технической эффективности / В. Я. Дзюзер, В. С. Швыдкий // Новые огнеупоры. ― 2015. ― № 12. ― С. 9‒12.]
27. Бах, X. Виды брака в производстве стекла / X. Бах, Ф. Г. К. Баукке, P. Брюкнер [и др.] ; под ред. Г. Иебсена-Марведеля, Р. Брюкнера ; сокр. пер. с нем. Л. Г. Вайбурт [и др.] ; под ред. Н. Н. Рохлина. ― М. : Стройиздат, 1986. ― 648 с.
28. Озеров, Н. А. Математическое моделирование высокотемпературной коррозии огнеупоров варочного бассейна стекловаренных печей / Н. А. Озеров, Б. А. Семенов, В. Н. Лункин // Изв. вузов. Проблемы энергетики. ― 2010. ― № 7/8. ― С. 88‒93.
29. Heidrich, R. REFEL 1616ULX ― an ultra-low exudation fused cast product for the super-structure of glass melting furnaces / R. Heidrich, A. Gupta, S. Postrach, M. Dietrich // RHI Bulletin. ― 2014. ― № 2. ― P. 16—17.
30. Cabodi, I. ER 2001 SLX — very low exudation AZS product for glass furnace superstructures / I. Cabodi, M. Gaubil, C. Morand // Refractories Worldforum. ― 2011. ― Vol. 3, № 2. ― P. 83‒86.
Supplementary files
For citation: Dzyuzer V.Y. Analysis of quality parameters of fused cast AZS refractories for glass-making furnaces. NOVYE OGNEUPORY (NEW REFRACTORIES). 2021;(4):3-9. https://doi.org/10.17073/1683-4518-2021-4-3-9
Refbacks
- There are currently no refbacks.