Changing the structure of the surface layer of ceramic products during operation. Part 2

V. V. Kuzin; S. N. Grigor'ev; M. A. Volosova

doi:10.17073/1683-4518-2020-3-50-55

Changing the structure of the surface layer of ceramic products during operation. Part 2

V. V. Kuzin, S. N. Grigor'ev, M. A. Volosova

https://doi.org/10.17073/1683-4518-2020-3-50-55

Full Text:

Abstract

Kinetics of structure changes of surface layer of ceramic part outside the area of contact interaction during operation was studied with using original technique. The main regularities of this process are established and the influence of defect degree of initial surface layer on the changes occurring was revealed.

Keywords

ceramic products (CP), surface layer (SL) of ceramics, ceramic failure, contact interaction region, ceramic structural elements, stress-strain state, wear site, contact area (CA),

About the Authors

V. V. Kuzin

ФГБОУ ВО «Московский государственный технологический университет «Станкин»
Russian Federation

S. N. Grigor'ev

ФГБОУ ВО «Московский государственный технологический университет «Станкин»
Russian Federation

M. A. Volosova

ФГБОУ ВО «Московский государственный технологический университет «Станкин»
Russian Federation

References

1. Кузин, В. В. Изменение структуры поверхностного слоя керамических изделий при эксплуатации. Часть 1 / В. В. Кузин, С. Н. Григорьев, М. А. Волосова // Новые огнеупоры. ― 2020. ― № 2. ― С. 39‒45.

2. Кузин, В. В. Роль теплового фактора в механизме износа керамических инструментов. Часть 1. Макроуровень / В. В. Кузин, С. Н. Григорьев, М. А. Волосова // Трение и износ. ― 2014. ― № 6. ― С. 728‒734.

3. Kuzin, V. V. The role of the thermal factor in the wear mechanism of ceramic tools : Рart 1. Macrolevel / V. V. Kuzin, S. N. Grigoriev, M. A. Volosova // Journal of Friction and Wear. ― 2014. ― Vol. 35, № 6. ― Р. 505‒510.

4. Кузин, В. В. Роль теплового фактора в механизме износа керамических инструментов. Часть 2. Микроуровень / В. В. Кузин, С. Н. Григорьев, М. Ю. Федоров // Трение и износ. ― 2015. ― № 1. ― С. 50‒55.

5. Kuzin, V. V. Role of the thermal factor in the wear mechanism of ceramic tools. Part 2. Microlevel / V. V. Kuzin, S. N. Grigoriev, M. Yu. Fedorov // Journal of Friction and Wear. ― 2015. ― Vol. 36, № 1. ― Р. 40‒44.

6. Волосова, М. А. Закономерности изнашивания режущих пластин из оксидной и нитридной керамики / М. А. Волосова, В. В. Кузин // Металловедение и термическая обработка. ― 2012. ― № 1. ― С. 40‒46.

7. Volosova, M. A. Regular features of wear of cutting plates from oxide and nitride ceramics / M. A. Volosova, V. V. Kuzin // Met. Sci. Heat Treat. ― 2012. ― Vol. 54, № 1/2. ― Р. 41‒46.

8. Кузин, В. В. Износ инструментов из нитридной керамики при обработке никелевых сплавов / В. В. Кузин, М. А. Волосова, М. Ю. Федоров // Трение и износ. ― 2013. ― Т. 34, № 3. ― С. 265‒271.

9. Kuzin, V. V. Wear of tools from nitride ceramics when machining nickel-based alloys / V. V. Kuzin, M. A. Volosova, M. Yu. Fedorov // Journal of Friction and Wear. ― 2013. ― Vol. 34, № 3. ― Р. 199‒203.

10. Кузин, В. В. Особенности изнашивания и разрушения керамических режущих пластин / В. В. Кузин, В. Н. Аникин, С. Ю. Федоров [и др.] // Вестник машиностроения. ― 2010. ― № 11. ― С. 50‒56.

11. Kuzin, V. V. Wear and failure of ceramic cutting plates / V. V. Kuzin, V. N. Anikin, S. Yu. Fedorov [et al.] // Russian Engineering Research. ― 2010. ― Vol. 30, № 11. ― Р. 1116‒1123.

12. Kuzin, V. Tool life and wear mechanism of coated Si3N4 ceramic tools in turning grey cast iron / V. Kuzin, S. Grigoriev // Key Eng. Mater. ― 2014. ― Vol. 581. ― Р. 14‒17.

13. Kuzin, V. Surface defects formation in grinding of silicon nitride ceramics / V. Kuzin, S. Grigoriev, S. Fedorov [et al.] // Applied Mechanics and Materials. ― 2015. ― Vols. 752/753. ― Р. 402‒406.

14. Kuzin, V. V. Technology for machining high-refractory ceramic parts based on silicon nitride / V. V. Kuzin // Refract. Ind. Ceram. ― 2006. ― Vol. 47, № 4. ― P. 204‒208.

15. Кузин, В. В. Технология механической обработки деталей из высокоогнеупорной керамики на основе нитрида кремния / В. В. Кузин // Новые огнеупоры. ― 2006. ― № 8. ― С. 19‒24.

16. Кузин, В. В. Технологические особенности алмазного шлифования деталей из нитридной керамики / В. В. Кузин // Вестник машиностроения. ― 2004. ― № 1. ― С. 37‒41.

17. Kuzin, V. V. Technological aspects of diamond grinding of the nitride ceramics / V. V. Kuzin // Russian Engineering Research. ― 2004. ― Vol. 24, № 1. ― Р. 23‒28.

18. Kuzin, V. V. Introduction to ceramic micromechanics. Ceramic object operating system / V. V. Kuzin, S. N. Grigor’ev, V. N. Anikin // Refract. Ind. Ceram. ― 2019. ― Vol. 60, № 1. ― Р. 120‒123.

19. Кузин, В. В. Введение в микромеханику керамики. Система эксплуатации керамических изделий / В. В. Кузин, С. Н. Григорьев, В. Н. Аникин // Новые огнеупоры. ― 2019. ― № 2. ― С. 60‒64.

Supplementary files

For citation: Kuzin V.V., Grigor'ev S.N., Volosova M.A. Changing the structure of the surface layer of ceramic products during operation. Part 2. NOVYE OGNEUPORY (NEW REFRACTORIES). 2020;(3):50-55. https://doi.org/10.17073/1683-4518-2020-3-50-55

Refbacks

There are currently no refbacks.

ISSN 1683-4518 (Print)

Username
Password