Properties of Al2O3-based ceramics with the addition of ultrafine Al2O3 powder synthesized by electrochemical method
https://doi.org/10.17073/1683-4518-2019-7-28-30
Abstract
The results of studies of the regularity of sintering and properties of corundum-based ceramics with the addition of ultrafine powder (UFP) Al2O3 synthesized by electrochemical method are presented. It is shown that with an increase in the calcination temperature and the concentration of UFP Al2O3, a regular increase in linear shrinkage, microhardness and strength of ceramics is observed (the maximum values at 1550 °С are 27,8 %, 17 GPa and 340 MPa, respectively). The introduction of UFP Al2O3 allows even at a calcining temperature of 1550 °C to achieve an apparent ceramic density of 3,87 g/cm3. Ref. 12. Tab. 3.
About the Authors
Yu. I. KomolikovRussian Federation
I. D. Kashcheev
Russian Federation
K. G. Zemlyanoy
Russian Federation
V. I. Pudov
Russian Federation
References
1. Полубояринов, Д. Н. Керамика из высокоогнеупорных окислов / Д. Н. Полубояринов. ― М. : Металлургия, 1977. ― 304 с.
2. Павлушкин, Н. М. Спеченный корунд / Н. М. Павлушкин. ― М. : Стройиздат, 1961. ― 210 с.
3. Балкевич, В. Л. Техническая керамика / В. Л. Балкевич. ― М. : Стройиздат, 1984. ― 256 с.
4. Смирнов, В. В. Корундовая керамика с низкой температурой спекания / В. В. Смирнов, И. В. Синица // Огнеупоры. ― 1994. ― № 10. ― С. 7‒9. Smirnov, V. V. Corundum ceramics with a low sintering temperature / V. V. Smirnov, I. V. Sinitsa // Refractories. ― 1994. ― Vol. 35, № 10. ― Р. 322‒324.
5. Лукин, Е. С. Современная высокоплотная оксидная керамика с регулируемой микроструктурой. Ч. I. Влияние агрегации порошков оксидов на спекание и микроструктуру керамики / Е. С. Лукин // Огнеупоры и техническая керамика. ― 1996. ― № 1. ― С. 5‒14. Lukin, E. S. Modern high-density oxide ceramics with controlled microstructure. Part I. Effect of aggregation of oxide powders on the sintering and microstructure of ceramics / E. S. Lukin // Refract. Ind. Ceram. ― 1996. ― Vol. 37, № 1. ― Р. 6‒14.
6. Лукин, Е. С. Современная высокоплотная оксидная керамика с регулируемой микроструктурой. Ч. II. Обоснование принципов выбора добавок, влияющих на степень спекания оксидной керамики / Е. С. Лукин // Огнеупоры и техническая керамика. ― 1996. ― № 4. ― С. 2‒13. Lukin, E. S. Modern high-density oxide ceramics with controlled microstructure. Part II. Substantiation of the choice of modifying additives that affect the degree of sintering of oxide ceramics / E. S. Lukin // Refract. Ind. Ceram. ― 1996. ― Vol. 37, № 4. ― Р. 109‒119.
7. Лукин, Е. С. Новые виды корундовой керамики с добавками эвтектических составов / Е. С. Лукин, Н. А. Макаров, Н. А. Попова [и др.] // Конструкционные материалы. ― 2001. ― № 3. ― С. 5‒10.
8. Hsu, Y. F. Effects of additives on the densification and microstructural evolution of fine Al2O3 powder / Y. F. Hsu, S. F. Wang, T. W. Cheng // Mater. Sci. Eng. ― 2003. ― Vol. 362. ― P. 300‒308.
9. Sathiyakuman, M. Influence of additives on density, microstructure and mechanical properties of alumina / M. Sathiyakuman, F. B. Gnanam // J. Mater. Proces. Technol. ― 2003. ― Vol. 133. ― P. 282‒286.
10. Верещагин, В. И. Функциональная керамика / В. И. Верещагин, П. М. Плетнев, А. П. Суржиков, В. Е. Федоров. ― Новосибирск : Наука, 2004. ― 348 с.
11. Лотов, В. А. Кинетика спекания корундовой керамики с микродобавками / В. А. Лотов, А. Т. Добролюбов // Стекло и керамика. ― 1997. ― № 11. ― С. 10‒12.
12. Zeng, Wenming. Sintering kinetics of Al2O3 powder / Wenming Zeng, Lian Gao, Linhua Gui, Jinkun Guo // Ceram. Int. ― 1999. ― Vol. 25. ― P. 723‒726.
Supplementary files
For citation: Komolikov Y.I., Kashcheev I.D., Zemlyanoy K.G., Pudov V.I. Properties of Al2O3-based ceramics with the addition of ultrafine Al2O3 powder synthesized by electrochemical method. NOVYE OGNEUPORY (NEW REFRACTORIES). 2019;(7):28-30. https://doi.org/10.17073/1683-4518-2019-7-28-30
Refbacks
- There are currently no refbacks.