SHC pressing of TiC + xC composites
https://doi.org/10.17073/1683-4518-2019-9-42-45
Abstract
Experimental results of the preparation of refractory electrically conductive composites TiC + xC by SHS pressing are presented. The conditions for obtaining composites with a residual porosity of about 20 % are determined. The effect of the composition of the reaction mixture on the phase composition, microstructure, tensile strengths under compression and bending, and the electrical resistivity of SHS composites was studied. It was shown that the compressive and bending strength of composites based on the TiC + xC system is 80-100 and 100-150 MPa, respectively, which is 3-5 times higher than the strength of fine-grained graphite. The electrical resistivity of the composites corresponds to the electrical resistivity of fine-grained graphite (16-18 μOhm·m). Ill. 3. Ref. 11. Tab. 3.
About the Authors
V. A. ScherbakovRussian Federation
A. N. Gryadunov
Russian Federation
References
1. Уббелоде, А. Р. Графит и его кристаллические соединения / А. Р. Уббелоде, Ф. А. Льюис. — М. : Мир, 1965. — 256 с.
2. Селезнёв, А. М. Углеродистое сырье для электродной промышленности / А. М. Селезнёв. — М. : Профиздат, 2000. — 256 с.
3. Соседов, В. П. История развития углеродной промышленности / В. П. Соседов. — М. : Аспектпресс, 1999. — 264 с.
4. ONO, Т. Hot-pressing of TiC-graphite composite materials / T. Ono, H. Endo, M. Ueki // J. Mater. Eng. Perform. — 1993. — Vol. 2, № 5. — Р. 659-664. DOI: http://dx.doi.org/10.1007/BF02650054.
5. Epishin, K. L. Compaction of materials forming in self-propagating high-temperature synthesis / K. L. Epishin, A. N. Pityulin, A. G. Merzhanov // Soviet powder metallurgy and metal ceramics. — 1992. — Vol. 31, № 6. — Р. 472-476. DOI: http://dx.doi.org/10.1007/BF00802441.
6. Питюлин, A. H. Силовое компактирование в СВС процессах. Самораспространяющийся высокотемпературный синтез: теория и практика / А. Н. Питюлин. — Черноголовка : Территория, 2001. — С. 333-353.
7. Shiryaev, A. A. Thermodynamic of SHS: Modern approach / A. A. Shiryaev // Int. J. SHS. — 1995. — Vol. 4, № 4. — Р. 351-362.
8. Mamyan, S. S. Thermodynamic studies of the possibility of forming inorganic materials by SHS with a reduction stage / S. S. Mamyan, A. A. Shiryaev, A. G. Merzhanov // J. Eng. Phys. Thermophys. — 1993. — Vol. 65, № 4. — Р. 974-980. DOI: http://dx.doi.org/10.1007/BF00862769.
9. Мержанов, A. Г. Твердопламенное горение / А. Г. Мержанов. — Черноголовка : ИСМАН, 2000. — 224 с.
10. Shcherbakov, V. A. Synthesis and characteristics of B4C-TiB2 composite / V. A. Shcherbakov, A. N. Gryadunov, M. I. Alymov // Adv. Mater. Technol. — 2016. — № 4. — P. 16-21. DOI: http://dx.doi.org/10.17277/amt.2016.04.pp.016-021.
11. Щербаков, В. A. Макрокинетика процесса СВС-компактирования / В. А. Щербаков, А. Н. Грядунов, А. С. Штейнберг // Инженерно-физический журнал. — 1992. — Т. 63, № 5. — С. 583-592.
Supplementary files
For citation: Scherbakov V.A., Gryadunov A.N. SHC pressing of TiC + xC composites. NOVYE OGNEUPORY (NEW REFRACTORIES). 2019;(9):42-45. https://doi.org/10.17073/1683-4518-2019-9-42-45
Refbacks
- There are currently no refbacks.