Aluminosilicate lightweight materials based on cracked clay of the Angren field of Uzbekistan
https://doi.org/10.17073/1683-4518-2019-8-8-12
Abstract
The possibility of using crack clay of the Angrenskoye field for the production of lightweight refractories has been studied. The phase composition and properties of the initial raw materials and compositions based on them are determined. It has been shown that the optimal combination of physicotechnical properties (compressive strength 7-10 MPa, apparent density 1,1-1,2 g/cm3) is possessed by samples of lightweight refractory products based on crack clay containing 20-40 wt. % black carbonaceous clay with a fading additive in the form of coke. Ill. 7. Ref. 18. Tab. 1.
About the Authors
M. Kh. RumiUzbekistan
Sh. K. Irmatova
Uzbekistan
Sh. A. Fayziev
Uzbekistan
M. A. Zufarov
Uzbekistan
E. P. Mansurova
Uzbekistan
E. M. Urazaeva
Uzbekistan
G. M. Arushanov
Uzbekistan
References
1. Стрелов, К. К. Технология огнеупоров / К. К. Стре-лов, П. С. Мамыкин. — М. : Металлургия, 1978. — 376 с.
2. Дудеров И. Г. Общая технология силикатов : учебник для техникумов / И. Г Дудеров. — М. : Стройиздат, 1987. — 560 с.
3. Сидоренко А. В. Геология СССР. Т IV. Центр Европейской части СССР (Московская, Владимирская, Ивановская, Калининская, Калужская, Костромская, Рязанская, Тульская, Смоленская и Ярославская области). Полезные ископаемые / А. В. Сидоренко. — М. : Недра, 1974. — 200 с.
4. Солодкий, Н. Ф. Минерально-сырьевая база Урала для керамической, огнеупорной и стекольной промышленности : справочное пособие / Н. Ф. Солодкий, А. С. Шамриков, В. М. Погребенков ; под ред. проф. Г. Н. Масленниковой. — Томск : Изд-во ТПУ, 2009. — 332 с.
5. Amkpa, J. A. Influence of sintering temperatures on physico-mechanical properties and microstructure of refractory fireclay bricks / J. A. Amkpa, N. A. Badarulzaman, A. B. Aramjat // International Journal of Engineering and Technology (IJET). — Dec. 2016 / Jan. 2017. — Vol. 8, № 6. — P. 2588-2593.
6. Kawamura, Junichi. Effect of particle-size distribution on characteristics of castable refractory / Junichi Kawamura, Kisaburo Ariyoshi, Teruo Yoshikata, Masakatsu Yamasaki // Journals Free Access. — 1977. — Vol. 85, № 979. — P. 101-110. https://www.jstage.jst.go.jp/article/jcersj1950/85/979/85_979_101/_article/-char/en
7. Вольфкович, С. И. Общая химическая технология / С. И. Вольфкович, А. П. Егоров, З. А. Роговин [и др.] ; под ред. С. И. Вольфковича. — М. : Изд-во химической литературы, 1959. — 848 с.
8. Пат. 2148566 Российская Федерация. Шихта для производства шамотных изделий и способ приготовления огнеупоров / Шатохин И. М. ; заявитель и патентообладатель — Шатохин И. М. — № 98114666/03 ; заявл. 11.08.98 ; опубл. 10.05.00, Бюл. № 13.
9. Коновалова, О. А. Алюмосиликатные огнеупоры на основе минерального сырья Западной Сибири : автореферат диссертации на соискание ученой степени кандидата технических наук / О. А. Коновалова. — Томск, 2002. — 19 с.
10. Sennikov, S. G. Use of the carbonaceous clay from the Latnenskoe deposit / S. G. Sennikov, M. V. Sennikova, S. M. Emtsova [et al.] // Refract. Ind. Ceram. — 1997. — Vol. 38, № 11/12. — P. 460-462.
11. Stolboushkin, A. The investigation of the matrix structure of ceramic brick made from carbonaceous mudstone tailings / A. Stolboushkin, O. Fomina, A. Fomin // IOP Conf. Series: Materials Science and Engineering. — 2016. — 124 012143 doi:10.1088/1757-899X/124/1/012143. https://www.researchgate.net/publication/301571099
12. Будников, П. П. Влияние минерализаторов на процесс муллитизации глин, каолинов и синтетических масс / П. П. Будников // Журнал прикладной химии. — 1946. — Т. 19, № 10/11. — С. 230.
13. Полубояринов, Д. Н. Керамика из высокоогнеупорных окислов / Д. Н. Полубояринов. — М. : Металлургия, 1977. — 304 с.
14. Chen, Chin-Yi. Evolution of mullite texture on firing tape-cast kaolin bodies / Chin-Yi Chen, Tuan Wei-Hsing // J. Am. Ceram. Soc. — 2002. — № 5. — P. 1121-1126 http://ntur.lib.ntu.edu.tw/bitstream/246246/95442/1/37.pdf
15. Chen, C. Y. Microstructural evolution of mullite during the sintering of kaolin powder compacts / C. Y. Chen, G. S. Lan, W. H. Tuan // Ceram. Int. — 2000. — № 26. — P. 715-720. https://pdfs.semanticscholar.org/092e/e5b1ea4fba1ac960293e4c31606a1dccb897.pdf
16. Martin-Marquez, J. Mullite development on firing in porcelain stoneware bodies / J. Martin-Marquez, J. Ma. Rincon, M. Romero // J. Eur. Ceram. Soc. — 2010. — Vol. 30, № 7. — P. 1599-1607. doi:10.1016/j.jeurceramsoc.2010.01.002 http://digital.csic.es/bitstream/10261/134268/1/Journal%20of%20the%20European%20Ceramic%20Society%2030,%20%207,%20%202010,%20%201599%E2%80%931607.pdf
17. Xiang, Wang. Emulsion-templated high porosity mullite ceramics with sericite induced textured structures / Xiang Wang, Jin-hong Li, Wei-min Guan [et al.] // Mater. Des. — 2016. — Vol. 89. — P. 1041-1047. http://www.cugb.edu.cn/uploadCms/file/20600/papers_upload/2016100817412722017.pdf
18. Милейко, С. Т. Монокристаллические волокна муллита, получаемые методом внутренней кристаллизации / С. Т. Милейко, А. В. Серебряков, В. М. Кийко [и др.] // Композиты и наноструктуры. — 2009. — № 2. — С. 47-60.
Supplementary files
For citation: Rumi M.K., Irmatova S.K., Fayziev S.A., Zufarov M.A., Mansurova E.P., Urazaeva E.M., Arushanov G.M. Aluminosilicate lightweight materials based on cracked clay of the Angren field of Uzbekistan. NOVYE OGNEUPORY (NEW REFRACTORIES). 2019;(8):8-12. https://doi.org/10.17073/1683-4518-2019-8-8-12
Refbacks
- There are currently no refbacks.