Preparation and properties of melted zircon
https://doi.org/10.17073/1683-4518-2019-5-96-99
Abstract
The data on the melting of zircon with the addition of glassforming oxides are given. The structure of the synthesized materials is represented by baddeleite and glass phase, which determine the operational characteristics of the refractory. Corrosion tests of samples of melted zircon in molten aluminum alloys showed their zero wettability and minimal corrosion. The material with an less than 2 % SiO2 was obtained when melted zircon was treated with a solution of 10 % HF. The threefold decrease in the silica content in the melting product was observed in electric arc furnace with carbothermic melting of zircon.
About the Authors
V. A. SokolovRussian Federation
M. D. Gasparyan
Russian Federation
E. V. Bogatyreva
Russian Federation
References
1. Гаспарян, М. Д. Опытно-промышленная установка ЭДП-600М для плавки тугоплавких оксидных материалов / М. Д. Гаспарян, В. А. Соколов // Энергосберегающие технологии в промышленности. Печные агрегаты. Экология : сб. науч. тр. Междунар. конф. (15‒20 октября 2012 г.). ― М. : Изд-во ООО «ИТЕП», НИТУ МИСИС». ― 2012. ― С. 117, 118.
2. Соколов, В. А. Разработка экологически безопасного получения диоксида циркония из цирконового концентрата / В. А. Соколов, С. В. Махов, Е. В. Богатырева // Мат-лы междунар. науч.-практ. конф. «Интенсификация гидрометаллургических процессов переработки природного и техногенного сырья. Технологии и оборудование». Санкт-Петербург, 28 мая ‒ 1 июня 2018 г. ― С. 302‒304.
Supplementary files
For citation: Sokolov V.A., Gasparyan M.D., Bogatyreva E.V. Preparation and properties of melted zircon. NOVYE OGNEUPORY (NEW REFRACTORIES). 2019;1(5):96-99. https://doi.org/10.17073/1683-4518-2019-5-96-99
Refbacks
- There are currently no refbacks.