Physico-mechanical characteristics and phase composition of unburned periclase-carbon refractories on modified phenol-formaldehyde resin
https://doi.org/10.17073/1683-4518-2019-3-29-33
Abstract
The possibilities of improving the physico-mechanical properties of periclase-carbon materials by modifying the phenol-formaldehyde resin (PFR) with organoinorganic complexes are described. The composition of the modifying additives, the phase composition of the materials after the PFR hardening are given, the influence of modifiers on the formation of the structure of materials is established. It is shown that the introduction of ethyl silicate or hydrolyzed ethyl silicate into liquid PFR during preparation of the charge contributes to the formation of SiC in the phase composition. The conclusion is made about the rationality of the introduction of ethyl silicate in an amount of from 0,66 to 1 wt. % and the prospects of introducing nickel oxalate into a liquid PFR together with ammonium citrate to increase the compressive strength of periclase-carbon materials up to 60 MPa. Ill. 7. Ref. 9.
About the Authors
D. A. BrazhnikUkraine
G. D. Semchenko
Ukraine
G. N. Shabanova
Ukraine
E. E. Starolat
Ukraine
I. N. Rozhko
Ukraine
L. V. Rudenko
Ukraine
References
1. Аксельрод, Л. М. Развитие производства огнеупоров в мире и в России, новые технологии / Л. М. Аксельрод // Новые огнеупоры. ― 2011. ― № 3. ― С. 106‒119. Aksel’rod, L. M. Development of refractory production in the world and in Russia, new technologies / L. M. Aksel’rod // Refract. Ind. Ceram. ― 2011. ― Vol. 52, № 2. ― Р. 95‒108.
2. Кащеев, И. Д. Исследование структуры и свойств графитов для производства огнеупоров. Часть 2. Свойства периклазо- и корундоуглеродистых огнеупоров при введении в их состав графитов различных производителей / И. Д. Кащеев, К. Г. Земляной, С. А. Поморцев // Новые огнеупоры. ― 2016. ― № 1. ― С. 17‒21. Kashcheev, I. D. Study of the structure and properties of graphites for refractory production. Part 2. Properties of periclase and corundum-graphite refractories with introduction into their composition of graphite from different producers / I. D. Kashcheev, K. G. Zemlyanoi, S. A. Pomortsev // Refract. Ind. Ceram. ― 2016. ― Vol. 57, № 1. ― Р. 22‒26.
3. Кащеев, И. Д. Армирование углеродистыми волокнами периклазоуглеродистых огнеупоров / И. Д. Кащеев, К. Г. Земляной, С. А. Поморцев [и др.] // Новые огнеупоры. ― 2015. ― № 12. ― С. 18‒20. Kashcheev, I. D. Periclase-carbon refractory reinforcement with carbon fibers / I. D. Kashcheev, K. G. Zemlyanoi, S. A. Pomortsev // Refract. Ind. Ceram. ― 2016. ― Vol. 56, № 6. ― P. 641‒643.
4. Вислогузова, Э. А. Анализ влияния качества периклазоуглеродистых огнеупоров на стойкость футеровки конвертеров / Э. А. Вислогузова, И. Д. Кащеев, К. Г. Земляной // Новые огнеупоры. ― 2013. ― № 3. ― C. 129‒133. Visloguzova, Е. A. Analysis of the effect of periclasecarbon refractory quality on converter lining life / Е. A. Visloguzova, I. D. Kashcheev, K. G. Zemlyanoi // Refract. Ind. Ceram. ― 2013. ― Vol. 54, № 2. ― P. 83‒87.
5. Кащеев, И. Д. Влияние алюмомагниевого антиоксиданта на свойства периклазоуглеродистых изделий / И. Д. Кащеев, С. А. Поморцев // Новые огнеупоры. ― 2012. ― № 8. ― C. 17‒20. Kashcheev, I. D. Effect of aluminum-magnesium antioxidant on periclase-carbon object properties / I. D. Kashcheev, S. A. Pomortsev // Refract. Ind. Ceram. ― 2012. ― Vol. 53, № 4. ― Р. 238‒241.
6. Семченко, Г. Д. Синтез и превращения при нагревании органического прекурсора никельсодержащего антиоксиданта для периклазоуглеродистых огнеупоров / Г. Д. Семченко, Д. А. Бражник, В. В. Повшук [и др.] // Новые огнеупоры. ― 2016. ― № 1. ― С. 29‒34. Semchenko, G. D. Synthesis and conversion on peating of nickel-containing antioxidant organic precursor for periclase-carbon refractories / G. D. Semchenko, D. A. Brazhnik, V. V. Povshuk [et al.] // Refract. Ind. Ceram. ― 2016. ― Vol. 57, № 1. ― Р. 33‒37.
7. Патент 79197 Украина, НПК 7 С 04 В 35/035, С 04 В 35/622, С 04 В 35/04, С 03 В 35/63. Способ изготовления магнезиально-углеродистых огнеупоров / Семченко Г. Д., Слепченко О. Н., Соловей Т. В. ― № а 2005 09045 ; заявл. 26.09.05 ; опубл. 25.05.07, Бюл. № 7.
8. Семченко, Г. Д. Наноупрочненные периклазоуглеродистые огнеупоры / Г. Д. Семченко, О. Н. Борисенко, В. В. Повшук. ― Харьков : Радуга, 2012. ― 128 с.
9. Семченко, Г. Д. Золь-гель композиции полифункционального назначения / Г. Д. Семченко, И. Ю. Шутеева, А. Н. Бутенко [и др.]. ― Харьков : Радуга, 2011. ― 240 с
Supplementary files
For citation: Brazhnik D.A., Semchenko G.D., Shabanova G.N., Starolat E.E., Rozhko I.N., Rudenko L.V. Physico-mechanical characteristics and phase composition of unburned periclase-carbon refractories on modified phenol-formaldehyde resin. NOVYE OGNEUPORY (NEW REFRACTORIES). 2019;(3):29-33. https://doi.org/10.17073/1683-4518-2019-3-29-33
Refbacks
- There are currently no refbacks.