Researches in the field of composite HCBS and of the refractory materials on their base in Al2O3‒SiO2‒SiC system. Part 4
https://doi.org/10.17073/1683-4518-2019-3-21-27
Abstract
The effect of long heat treatment (single and double firing in a tunnel kiln) of samples based on a HBCS in Al2O3‒ SiO2‒SiC-system on their indicators was studied. Samples containing 15 % SiC and 1 and 2 % Si are characterized by a significant increase (up to 9 %) an increase in porosity and a decrease in strength compared to the original samples (without SiC) after long heat treatment (120 hours in the range of 1300‒1400 oC). A significant increase in the volume of the samples is due not only to the oxidation of SiC or Si, but also to additional mullite formation. It is assumed that sequentially following the process of oxidation of SiC at a certain stage of heat treatment, the process of mullitization proceeds due to the interaction of the newly formed SiO2 in the form of cristobalite with Al2O3 bauxite. Ill. 6. Ref. 19.
About the Authors
Yu. E. PivinskiiRussian Federation
P. V. Dyakin
Russian Federation
References
1. Дякин, П. В. Исследования в области композиционных ВКВС и огнеупорных материалов на их основе в системе Al2O3‒SiO2‒SiC. Часть 3 / П. В. Дякин, Ю. Е. Пивинский, А. Ю. Колобов // Новые огнеупоры. ― 2018. ― № 9. ― C. 14‒22.
2. Пивинский, Ю. Е. Исследования в области композиционных ВКВС и огнеупорных материалов на их основе в системе Al2O3‒SiO2‒SiC. Часть 2 / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2018. ― № 5. ― C. 22‒27. Pivinskii, Yu. E. Research in the field of composite materials based on HCBS and refractory materials based on the system Al2O3‒SiO2‒SiC. Part 2 / Yu. E. Pivinskii, P. V. Dyakin // Refract. Ind. Ceram. ― 2018. ― Vol. 59, № 3. ― P. 247‒251.
3. Пивинский, Ю. Е. Исследования в области композиционных ВКВС и огнеупорных материалов на их основе в системе Al2O3‒SiO2‒SiC. Часть 1 / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2018. ― № 3. ― C. 17‒27. Pivinskii, Yu. E. Research in the field of composite materials based on HCBS and refractory materials based on the system Al2O3‒SiO2‒SiC. Part 1 / Yu. E. Pivinskii, P. V. Dyakin // Refract. Ind. Ceram. ― 2018. ― Vol. 59, № 2. ― P. 124‒133.
4. Кащеев, И. Д. Химическая технология огнеупоров / И. Д. Кащеев, К. K. Стрелов, П. С. Мамыкин. ― М. : Интермет Инжиниринг, 2007. ― 752 с.
5. Гнесин, Г. Г. Карбидокремниевые материалы / Г. Г. Гнесин. ― М. : Металлургия, 1977. ― 215 с.
6. Кайнарский, И. С. Карборундовые огнеупоры / И. С. Кайнарский, Э. В. Дегтярева. ― Харьков : Металлургия, 1963. ― 252 с.
7. Luz, A. P. Refractory castable engineering / A. P. Luz, M. A. J. Braulio, V. C. Pandolfelli. ― Baden-Baden : Goller Verlag GmbH, Germany, 2015. ―734 p.
8. Bo, Ren. Effects of oxidation of SiC aggregates on the microstructure and properties of bauxite ‒ SiС composite refractories / Ren Bo, Sang Shaobai, Li Yawei, Xu Yibiao // Ceram. Int. ― 2015. ― Vol. 41. ― P. 2892‒2899.
9. Roy, J. Oxidation behavior of silicon carbide ― a review / J. Roy, S. Chandra, S. Das, S. Maitra // Rev. Adv. Mater. Sci. ― 2014. ― Vol. 38. ― Р. 29‒39.
10. Zaidan, S. A. Effect nano-SiC additives in physical and mechanical properties of bauxite refractories used in oil units / S. A. Zaidan, H. H. Jasim // Eng. Technol. J. ― 2017. ― Vol. 35, Part A, № 10. ― Р. 992‒998.
11. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 14. Состав и некоторые свойства керамобетонов композиционного состава в системе Al2O3‒SiO2‒SiC‒С / Ю. Е. Пивинский, П. В. Дякин, Л. В. Остряков // Новые огнеупоры. ― 2018. ― № 2. ― С. 24‒31. Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 14. Composition and some properties of composite composition ceramic concretes in the system Al2O3‒SiO2‒SiC‒C / Yu. E. Pivinskii, P. V. Dyakin, L. V. Ostryakov // Refract. Ind. Ceram. ― 2018. ― Vol. 59, № 1. ― P. 63‒70.
12. Гришпун, Е. М. Производство и служба высокоглиноземистых керамобетонов. 1. Набивные массы на основе модифицированных ВКВС боксита / Е. М. Гришпун, Ю. Е. Пивинский, Е. В. Рожков [и др.] // Огнеупоры и техническая керамика. ― 2000. ― № 3. ― С. 37‒41. Grishpun, E. M. Production and service of highalumina ceramic castables. 1. Ramming mixtures based on modified bauxite HCBS / E. M Grishpun, Yu. E. Pivinskiy, E. V. Rozhkov [et al.] // Refract. Ind. Ceram. ― 2000. ― Vol. 41, № 5. ― Р. 104‒108.
13. Рожков, Е. В. Производство и служба высокоглиноземистых керамобетонов. 2. Свойства и служба виброналивных желобных масс на основе модифицированных ВКВС боксита / Е. В. Рожков, Ю. Е. Пивинский, М. З. Нагинский [и др.] // Огнеупоры и техническая керамика. ― 2001. ― № 5. ― C. 37‒44. Rozhkov, E. V. Production and service of highalumina castables. 2. Properties and service of vibrationplaced castables based on bauxite-modified highly concentrated ceramic binding suspensions (HCBS) for use in blast-furnace runners / E. V. Rozhkov, Yu. E. Pivinskii, M. Z. Naginskii [et al.] // Refract. Ind. Ceram. ― 2001. ― Vol. 42, № 5/6. ― Р. 209‒215.
14. Masakszu, Lida. Effect of SiC oxidation on corrosion resistance of castable for metal line of blast furnace main trough / Lida Masakszu, Eizo Maeda, Tsuyoshi Okamoto // Taikabutsu Overseas. ― 2007. ― Vol. 27, № 2. ― P. 90‒95.
15. Перепелицын, В. А. Фазовые превращения бетонов системы Al2O3‒SiC‒С при испытании на шлакоустойчивость / В. А Перепелицын, Л. В. Остряков, М. Н. Дунаева, А. Ю. Колобов // Новые огнеупоры. ― 2018. ― № 7. ― C. 29‒37. Perepelitsyn, V. A. Phase transformations of concrete of the Al2O3‒SiC‒C system during slag resistance testing / V. A. Perepelitsyn, L. V. Ostryakov, M. N. Dunaeva, A. Yu. Kolobov // Refract. Ind. Ceram. ― 2018. ― Vol. 59, № 4. ― Р. 350‒358.
16. Wei, Zhang. Research on thermal shock resistance of mullite ‒ bauxite ‒ silicon carbide refractory / Zhang Wei, Day Wenyong, Nobuaki Chiyoda // Chin. J. Geochem. ― 2012. ― Vol. 31. ― P. 204‒208.
17. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 4. Влияние добавок огнеупорной глины на свойства ВКВС композиционного состава, отливок и материалов на их основе / Ю. Е. Пивинский, П. В. Дякин // Новые огнеупоры. ― 2016. ― № 2. ― C. 25‒33. Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on highalumina HCBS. Part 4. Effect of refractory clay addition on properties of compaund composition HCBS, castigs and matеrials based on them / Yu. E. Pivinskii, P. V. Dyakin // Refract. Ind. Ceram. ― 2016. ― Vol. 57, № 1. ― P. 70‒76.
18. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 5. Влияние температуры обжига на свойства материалов, полученных из композиционных ВКВС с добавкой огнеупорной глины / Ю. Е. Пивинский, П. В. Дякин, Л. В. Остряков // Новые огнеупоры. ― 2016. ― № 4. ― C. 24‒29. Pivinskii, Yu. E. Research in the Field of preparing molded and unmolded refractories based on highalumina HCBS. Part 5. Effect of firing temperature on properties of materials prepared from composite HCBS with addition of refractory clay / Yu. E. Pivinskii, P. V. Dyakin, L. V. Ostraykov // Refract. Ind. Ceram. ― 2016. ― Vol. 57, № 2. ― P. 180‒184.
19. Пивинский, Ю. Е. Исследования в области получения формованных и неформованных огнеупоров на основе высокоглиноземистых ВКВС. Часть 13. Влияние температуры обжига на фазовый состав, структуру и некоторые свойства материалов на основе ВКВС композиционного состава: боксит, электрокорунд, кварцевое стекло / Ю. Е. Пивинский, В. А. Перепелицын, П. В. Дякин [и др.] // Новые огнеупоры. ― 2017. ― № 12. ― С. 27‒35. Pivinskii, Yu. E. Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 13. Effect of firing temperature on phase composition, structure, and some properties of materials based on composite composition HCBS (bauxite, electrocorundum, quartz glass) / Yu. E. Pivinskii, V. A. Perepelitsyn, P. V. Dyakin [et al.] // Refract. Ind. Ceram. ― 2018. ― Vol. 58, № 6. ― Р. 652‒659.
Supplementary files
For citation: Pivinskii Y.E., Dyakin P.V. Researches in the field of composite HCBS and of the refractory materials on their base in Al2O3‒SiO2‒SiC system. Part 4. NOVYE OGNEUPORY (NEW REFRACTORIES). 2019;(3):21-27. https://doi.org/10.17073/1683-4518-2019-3-21-27
Refbacks
- There are currently no refbacks.