The study of compositions based on parkent kaolin clay
https://doi.org/10.17073/1683-4518-2018-11-29-33
Abstract
The results of studies of the structure and composition of compositions based on red-burning kaolinite clay and calcium carbonate, heat-treated at 500 oC, in the process of acid activation are presented. It is shown that when a 12 % solution of H2SO4 is applied, leaching of iron and aluminum ions and the formation of calcium sulfate occur while maintaining the structure of kaolinite. The introduction of liquid glass into the composition of the material leads to the destruction of the structure of kaolinite, which contributes to an increase in the rate of extraction of aluminum ions during the subsequent acid activation. The components of the compositions with Ca2+ and Fe3+ in the presence of liquid glass are passivated by active amorphous silica formed during the reaction of liquid glass with CO2 air.Ill. 2. Ref. 17. Tab. 1.
About the Authors
M. Kh. RumiUzbekistan
Sh. K. Irmatova
Uzbekistan
M. A. Zufarov
Uzbekistan
Sh. A. Fayziev
Uzbekistan
E. P. Mansurova
Uzbekistan
E. M. Urazaeva
Uzbekistan
Sh. R. Nurmatov
Uzbekistan
References
1. Пат. 2137733 Российская Федерация. Способ получения упрочняющего покрытия на огнеупорных материалах / Владимиров В. С., Жуков Н. И., Мальцев В. М., Уваров Л. А., Хотенко С. В. ; заявл. 15.01.97 ; опубл. 20.09.99. http://ru-patent.info/21/35-39/2137733.html.
2. Heah, C. Y. General properties of kaolin geopolymers / C. Y. Heah, H. Kamarudin, A. M. Bakri [et al.] // Adv. Sci. Lett. ― 2013. ― Vol. 19, № 1. ― P. 153‒156. http://www.aspbs.com/science/contents-science192013.html.
3. Soleimani, M. A. Effect of calcination temperature of the kaolin and molar Na2О/SiO2 activator ratio on physical and microstructural properties of metakaolin based geopolymers / M. A. Soleimani, R. Naghizadeh, A. R. Mirhabibi, F. Golestanifard // Received : May 2012 Accepted: October 2012 School of Materials Science and Engineering, Iran University of Science and Technology, Tehran, Iran. http://ijmse.iust.ac.ir/browse.php?a_id=504&sid=1&slc_lang=en
4. Лоухина, И. В. Механическая активация каолинита серной кислотой : автореф. дис. ... канд. хим. наук. ― Сыктывкар, 2006. ― 145 с. http://www.dslib.net/tverdoe-sostojanie/mehanohimicheskoe-razlozheniekaolinita-sernoj-kislotoj.html.
5. Cмирнов, К. В. Разработка композиционных материалов на основе соединений силиката натрия и каолина : дис. ... канд. техн. наук. ― Иваново, 2007 ― 190 с. http://www.dslib.net/texnologia-neorganiki/razrabotka-kompozicionnyh-materialov-na-osnovesoedinenij-silikata-natrija-i.html.
6. Davidovits, J. Geopolymer chemistry and applications / J. Davidovits. ― Saint Quentin, France : Geopolymer Institute, 2008. ― P. 585. https://www.geopolymer.org/fchiers_pdf/GPCement2013.pdf.
7. Руми, М. Х. Глины Узбекистана как сырьевой материал для получения защитных покрытий на стальных поверхностях / М. Х. Руми, Ш. Р. Нурматов, Ш. К. Ирматова [и др.] // Огнеупоры и техническая керамика. ― 2017. ― № 1/2. ― С. 45‒48. http://refractory-journal.ru/arhiv2017_1-2.
8. Насыров, Р. Возможности применения методов ЭПР, ИК-спектроскопии и рентгеновской дифрактометрии при изучении геологического разреза нефтегазовых скважин /Р. Насыров, А. П. Слюсарев, И. Б. Саматов[и др.] // Изв. НАН РК. Сер. геологическая. ― 2008. ― № 5.― С. 50‒57. http://nauka-nanrk.kz/ru/asets/%D0%B6%D1%83%D1%80%D0%BD%D0%B0%D0%BB%202017%205/%D0%93%D0%B5%D0%BE%D0%BB%D0%BE%D0%B3%D0%B8%D1%8F__05_2017__%D0%93%D0%BE%D1%82%D0%BE%D0%B2.pdf.
9. Database ATR-FT-IR-spectra of various material / ATRFT-IR-spectra of kaolinite (Al2O3·2SiO2·2H2O). http://lisa.chem.ut.ee/IR_spectra/paint/fllers/kaolinite/.
10. Шишелова, Т. И. Практикум по спектроскопии. Вода в минералах : уч. пособие / Т. И. Шишелова, Т. В. Созинова, А. Н. Коновалова. ― М. : Академия естествознания, 2010. ― 88 с. https://monographies.ru/ru/book/view?id=74.
11. Antsiferov, V. N. Infulence of mechanochemical activation of a charge on properties of mullite-tialite materials / V. N. Antsiferov, S. E. Porozova, E. V. Matygullina // Science of Sintering. ― 2004. ― Vol. 36, № 1. ― P. 21‒26. http://www.doiserbia.nb.rs/img/doi/0350-820X/2004/0350-820X0401021A.pdf.
12. Шумков, А. И. Местные вяжущие, получаемые по энергосберегающим технологиям / А. И. Шумков // Изв. вузов. Строительство. ― 1993. ― № 11/12. ― С. 26‒30.
13. Тарасов, Р. В. Анализ возможности повышения термической стойкости материалов при комбинировании глин и шлаков в жаростойких композициях / Р. В. Тарасов, Л. В. Макарова, А. А. Батынова // Современные научные исследования и инновации. ― 2015. ― № 2. ― Ч. 2 [Электронный ресурс]. http://web.snauka.ru/issues/2015/02/46911.
14. Григорьев, П. Н. Растворимое стекло / П. Н. Григорьев, М. А. Матвеев. ― М. : Промстройиздат, 1956. ― 443 с. http://www.read.in.ua/book253334/?r=29&p=27.
15. Малявский, Н. И. Кальцийсиликатные отвердители жидкого стекла для получения водостойких щелочносиликатных утеплителей / Н. И. Малявский, В. В. Зверева // Интернет-вестник ВолгГАСУ. ― 2015. ― Вып. 2 (38). ― Ст. 5. www.vestnik.vgasu.ru.
16. Четверикова, А. Г. Исследования полиминеральной глины, содержащей трехслойные алюмосиликаты физическими методами / А. Г. Четверикова, В. С. Маряхина // Вестник Оренбургского государственного университета. ― 2015. ― № 1. ― С. 250‒255. https://cyberleninka.ru/article/n/issledovaniya-polimineralnoygliny-soderzhaschey-trehsloynye-alyumosilikatyfzicheskimi-metodami.17. Корнеев, В. И. Жидкое и растворимое стекло : производственное издание / В. И. Корнеев, В. В. Данилов. ― СПб. : Стройиздат, 1996. ― 216 с. https://www.chipmaker.ru/fles/fle/8454/.
Supplementary files
For citation: Rumi M.K., Irmatova S.K., Zufarov M.A., Fayziev S.A., Mansurova E.P., Urazaeva E.M., Nurmatov S.R. The study of compositions based on parkent kaolin clay. NOVYE OGNEUPORY (NEW REFRACTORIES). 2018;(11):29-33. https://doi.org/10.17073/1683-4518-2018-11-29-33
Refbacks
- There are currently no refbacks.