The influence of the admixture to the Al2O3‒MgO‒MnO system and of the firing temperature on the electro-fused corundum composite ceramics sintering
https://doi.org/10.17073/1683-4518-2018-7-20-23
Abstract
The influence of the eutectic composition addition to the Al2O3‒MgO‒MnO system on the structural ceramics' sintering was investigated in the article. The initial material was the electro-fused corundum F-1000 with the average particle size of 10 microns. The additive powder have been prepared in course of the thermolysis of the alumina hydroxyl together with the manganese carbonate and magnesia carbonate salts. The spinel MgO· Al2O3 and MnO· Al2O3 have been synthesized separately. It was established that when the addition contents was equal 15 weight percent after the burning at 1550 °С the ceramics density achieved 3,86 gram/cm3 the open porosity being 0,3 %, and the ultimate bent strength achieved 211 MPa.Ill.3. Ref. 8. Tab. 1.
About the Authors
Aung Chzho MoeRussian Federation
E. S. Lukin
Russian Federation
N. A. Popova
Russian Federation
References
1. Лукин, Е. С. Технология керамики на основе оксида алюминия, содержащей диоксид циркония / Е. С. Лукин, Н. А. Попова, Н. И. Здвижкова [и др.] // Огнеупоры. ― 1987. ― № 5. ― C. 8‒10.
2. Дабижа, А. А. Особенности технологии керамики на основе сталилизированного диоксида циркония / А. А. Дабижа, С. Ю. Плинер // Огнеупоры. ― 1986. ― № 11. ― C. 23‒29. [Dabizha, A. A. Strengthening ceramic materials due to phase inversion of ZrO2 (Reiew) / A. A. Dabizha, S. Yu. Pliner // Refractories. ― 1986. ― Vol. 27, № 11/12. ― P. 630‒636.]
3. Тонкая техническая керамика ; под ред. Х. Яногида; пер. с яп. ― М. : Металлургия, 1986. ― 278 с.
4. Лукин, Е. С. Прочная керамика на основе оксида алюминия и диоксида циркония / Е. С. Лукин, Н. А. Попова, Н. И. Здвижкова [и др.] // Стекло и керамика. ― 1993. ― № 9/10. ― C. 25‒29.
5. New Generation ceramic transmits light, processes great strength, resists extremely high temperatures // Ceram. Ind. ― 1959. ― Vol. 73, № 4. ― P. 57‒59.
6. Лукин, Е. С. О проблемах получения керамики с регулируемой структурой / Е. С. Лукин, Н. Т. Андрианов, Н. Б. Мамаева [и др.] // Огнеупоры. ― 1993. ― № 5. ― C. 11‒15. Lukin, E. S. Obtaining oxide ceramics with a regular structure / E. S. Lukin, N. T. Andrianova, N. B. Mamaeva [et al.] // Refractories. ― 1993. ― Vol. 34, № 5/6. ― P. 263‒267.
7. Павлушкин, Н. М. Спеченный корунд / Н. М. Павлушкин. ― М. : Стройиздат, 1961. ― 208 с.
8. Лукин, Е. С. Новые виды корундовой керамики с добавками эвтектических составов / Е. С. Лукин, Н. А. Макаров, Н. А. Попова [и др.] // Конструкция из конструкционных материалов. ― 2001. ― № 3. ― C. 28‒38.
Supplementary files
For citation: Moe A.C., Lukin E.S., Popova N.A. The influence of the admixture to the Al2O3‒MgO‒MnO system and of the firing temperature on the electro-fused corundum composite ceramics sintering. NOVYE OGNEUPORY (NEW REFRACTORIES). 2018;(7):20-23. https://doi.org/10.17073/1683-4518-2018-7-20-23
Refbacks
- There are currently no refbacks.