The investigation of the modified refractory concrete in terms of the clay filler's kind
https://doi.org/10.17073/1683-4518-2018-12-17-21
Abstract
The properties of the conventional refractory concrete modified by means of the microsilica and the antiflocculant additions including the different kinds of the fire clay filler were investigated in the article. It was established that the refractory concrete with the filler Bos145 (about 44 % of Al2O3) had the smaller open porosity, and both high density and the ultimate compressive strength comparing to these characteristics which the concretes with the fillers Bos125 and Bos135 had (about 26 and 37 % of Al2O3 respectively). Also it was found out that independently of the fire clay filler's kind another SiO2-based addition promoted the increase of the concrete's alkaline resistance by the factor of 5 and more. It was shown that this SiO2-based addition is effective at the temperatures up to 1100 °C, as at 1200 °C the chamotter concrete's porosity grew up and the resistance of the material against the alkaline melt decreased considerably.
About the Authors
P. ZdаnyavichusLithuania
V. Antonovich
Lithuania
R. Boris
Lithuania
R. Stonis
Lithuania
R. Shukis
Lithuania
E. Vitek
Poland
References
1. Антонович, В. Влияние дефлокулянта новой генерации и количества микрокремнезема на свойства традиционного жаростойкого бетона с шамотным заполнителем / В. Антонович, С. Гоберис, И. Пундене, Р. Стонис // Новые огнеупоры. ― 2006. ― № 5. ― С. 44‒48. [Antonovič, V. A new generation of deflocculants and microsilica used to modify the properties of a conventional refractory castable based on a chamotte filler / V. Antonovič, S. Goberis, I. Pundienė, R. Stonys// Refractories and Industrial Ceramics. ― 2006. ― Vol. 47, № 3. ― P. 178‒182.]
2. http://internet-law.ru/gosts/gost/58513/
3. Kerienė, J. Action of the products of biofuel combustion on the phase composition and structure of refractory material / J. Kerienė, R. Boris, V. Antonovič, R. Stonys, J. Škamat // Glass and ceramics. ― 2016. ― Vol. 72, № 9/10. ― Р. 345‒350.
4. Борис, Р. Исследование щелочной стойкости огнеупорных материалов, используемых в котлах, работающих на древесном топливе / Р. Борис, В. Антонович, Я. Керене [и др.] // Новые огнеупоры. ― 2016. ― № 12. ― С. 42‒45. [Boris, R. Study of alkali resistance of refractory materials used in boilers operating on wood fuel / R. Boris, V. Antonovič, J. Kerienė [et al.] // Refractories and Industrial Ceramics. ― 2017. ― Vol. 57, № 6. ― P. 651‒654.]
5. Alibasic, E. Design of castables and their relevance to alkali resistance applications / E. Alibasic, J. Oldin, S. Kannabiran, A. Yiakoum // 57th International Colloquium on Refractories, Eurogress. ― 2014. ― P. 67‒69.
6. Роучка, Г. Огнеупорные материалы. Структура, свойства, испытания : cправочник / Г. Роучка, Х. Вутнау, Й. Алленштейн ; под ред. Г. Роучка, Х. Вутнау ; пер. с нем. ― М. : Интермет Инжиниринг, 2010. ― С. 392.
7. Борис, Р. Исследование стойкости огнеупорных материалов к воздействию щелочных солей / Р. Борис, В. Антонович, Я. Керене [и др.] // Новые огнеупоры. ― 2016. ― № 3. ― С. 52, 53.
8. Szczerba, J. Badania oddziaływania soli alkaliów na beton wysokoglinowy bez i z dodatkami / J. Szczerba, A. Boczoń, B. Studencka// Ceramika. ― 2005. ― Vol. 88. ― P. 158‒172.
9. Antonovič, V. The effect of carbon and polypropylene fibers on thermal shock resistance of the refractory castable / V. Antonovič, J. Witek, R. Mačiulaitis [et al.] // Journal of Civil Engineering and Management. ― 2017. ― Vol. 23, № 5. ― P. 672‒678.
10. Гоберис, С. О некоторых особенностях пластифи-цирования низкоцементного жаростойкого бетона раствором силиката натрия / С. Гоберис, В. Антонович // Новые огнеупоры. ― 2004. ― № 9. ― С. 48‒51. [Goberis, S. Improving the structure and properties of a refractory castable containing porous chamotte fillers / S. Goberis, V. Antonovič // Refractories and Industrial Ceramics. ― 2004. ― Vol. 45, № 6. ― P. 446‒449.]
11. LST EN ISO 1927-5:2013 Monolithic (unshaped) refractory products – Part 5: Preparation and treatment of test pieces ; опубл. 2013.
12. LST EN ISO 1927-6:2013 Monolithic (unshaped) refractory products ‒ Part 6: Measurement of physical properties. ― Vilnius, 2013. ― 14 p.
13. ГОСТ 20910‒90:1991. Бетоны жаростойкие. Технические условия. ― Москва, 1991. ― 18 c.
14. LST EN ISO 10545-3:2000 Ceramic tiles ‒ Part 3: Determination of water absorption, apparent porosity, apparent relative density and bulk density. ― Vilnius, 2000. ― 6 p.
15. ASTM C 454-83:2007 Standard practice for disintegration of carbon refractories by alkali. American Technical Standard, 2007. ― 2 p.
16. ENISO 1893:2009 Refractory products - determination of refractoriness under load – differential method with rising temperature. International Standard Organization, 2009. 18 p.
17. Parr, C. The impact of calcium aluminate cement hydration upon the properties of refractory castable / C. Parr, F. Simonin, B. Touzo[et al.] // Kerneos Aluminate Technologies. Technical Paper. Reference TP-GB-RELAF-043. ― 2004. ― P. 17.
Supplementary files
For citation: Zdаnyavichus P., Antonovich V., Boris R., Stonis R., Shukis R., Vitek E. The investigation of the modified refractory concrete in terms of the clay filler's kind. NOVYE OGNEUPORY (NEW REFRACTORIES). 2018;(12):17-21. https://doi.org/10.17073/1683-4518-2018-12-17-21
Refbacks
- There are currently no refbacks.